  • IPEN-DOC 23161

    CUESTA, ANA; ICHIKAWA, RODRIGO U. ; LONDONO-ZULUAGA, DIANA; DE LA TORRE, ANGELES G.; SANTACRUZ, ISABEL; TURRILLAS, XAVIER; ARANDA, MIGUEL A.G.. Aluminum hydroxide gel characterization within a calcium aluminate cement paste by combined Pair Distribution Function and Rietveld analyses. Cement and Concrete Research, v. 96, p. 1-12, 2017. DOI: 10.1016/j.cemconres.2017.02.025

    Abstract: There are many commercially importantmultiphasematerialswhich contain amorphous phases, such as cement pastes, porcelains, glass-ceramics or pharmaceutical compounds. However, the analysis of amorphous phase(s) within cement matrices that contain high amounts of crystalline phase(s) is a challenge. Here, we report measurements of total scattering data quantitatively analyzed by Pair Distribution Function (PDF) minimization and Rietveld methodology to determine phase compositions including both amorphous and nanocrystalline phase contents in cement-related samples. Furthermore, laboratory techniques were used to complement the sample characterization. In addition to five reference materials, the main phase of calcium aluminate cements, CaAl2O4 hydrated at 50 °C to yield crystalline hydrogarnet, Ca3Al2(OH)12, (43wt%) and nanocrystalline aluminum hydroxide gel, Al(OH)3·0.1H2O (50wt%)was also investigated. The PDF analyses revealed that the hydroxide gel has a gibbsite local structurewith an average particle size close to 5 nm. PDF and Rietveld quantitative phase analysis results fully agree.

    Palavras-Chave: aluminium; hydroxides; gels; x-ray diffraction; calcium; aluminates; cements; garnets; amorphous state

  • IPEN-DOC 19883

    ICHIKAWA, RODRIGO U. . Aplicações do método Warren-Averbach de análise de perfis de difração / Applications of the Warren-Averbach method of X-ray diffraction line profile analysis . 2013. Dissertação (Mestrado) - Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP, São Paulo. 94 p. Orientador: Luis Gallego Martinez. DOI: 10.11606/D.85.2013.tde-10012014-103427

    Abstract: O objetivo deste trabalho foi desenvolver e implementar uma metodologia envolvendo a análise de perfis de difração de raios X (X-ray Line Profile Analysis - XLPA) para o estudo e determinação do tamanho médio de cristalitos e microdeformação em materiais. Para isto houve o desenvolvimento de um programa computacional para facilitar o tratamento dos picos presentes em um difratograma e realizar a deconvolução de perfis através do Método de Stokes para se corrigir a contribuição instrumental nos perfis de difração. Os métodos de XLPA de espaço real estudados e aplicados neste trabalho foram os métodos de Scherrer, Williamson-Hall e Single-Line (ou Linha Única) e o método de Warren-Averbach de espaço de Fourier. Além disso, utilizando-se um modelamento matemático foi possível calcular a distribuição de tamanhos de cristalitos para um caso isotrópico, onde considerou-se a distribuição log-normal e cristalitos com forma esférica. Foi possível demonstrar que a teoria proposta pode ser considerada como uma boa aproximação avaliando-se uma razão de dispersão. As metodologias descritas acima foram aplicadas em dois materiais distintos: na liga metálica Zircaloy-4 e em ZnO.

    Palavras-Chave: crystallography; fourier analysis; chemical analysis; x-ray diffraction; microstructure; zircaloy; yttrium oxides; zinc oxides; computer codes

  • IPEN-DOC 20231

    ANTUNES, RENATO A.; ICHIKAWA, RODRIGO U. ; MARTINEZ, LUIS G. ; COSTA, ISOLDA . Characterization of corrosion products on carbon steel exposed to natural weathering and to accelerated corrosion tests. International Journal of Corrosion, v. 2014, p. 419570-1 - 419570-9, 2014.

    Palavras-Chave: carbon steels; corrosion products; weathering; corrosion resistance; x-ray diffraction; moessbauer effect; raman spectroscopy; scanning electron microscopy

  • IPEN-DOC 24312

    ICHIKAWA, RODRIGO U. ; YOSHITO, WALTER K. ; SAEKI, MARGARIDA J.; MARANHAO, WILLIAN C.A. ; GOULART, FATIMA ; MARTINEZ, LUIS G. . Characterization of Mn0.67Zn0.33Fe2O4 nanoparticles synthesized under different pH. Materials Science Forum, v. 899, p. 48-53, 2017. DOI: 10.4028/www.scientific.net/MSF.899.48

    Abstract: Nanostructured Mn-Zn ferrites were synthesized using co-precipitation in alkaline solution with different pH. The samples were characterized using X-ray diffraction (XRD), X-ray fluorescence (XRF), thermal analysis (TG-DTA), dynamic light scattering (DLS) and scanning electron microscopy (SEM) techniques. Monophasic nanoparticles were formed when synthesized with pH 10.5. This sample was heat-treated and its XRD data was refined by the Rietveld method. Mean crystallite sizes and microstrains were determined from X-ray line profile analysis using Single-Line and Warren-Averbach methods, which revealed a mean crystallite size of approximately 10 nm and negligible microstrains. Zn content was estimated using refined cell parameters, giving a value of 33 at %, in accordance with XRF result. TG-DTA revealed that the incorporation of α-Fe2O3 occurs around 1130 °C and 1200 °C with recrystallization of the Mn-Zn ferrite spinel phase. DLS showed that mean particle size increase with temperature up to 1159 nm at 800 °C. SEM analysis showed the samples agglomerate and present similar morphology with negligible size changing when calcined between 280 °C and 800 °C. However, the sample calcined at 1200 °C presents larger agglomerates due to the sintering process.

    Palavras-Chave: manganese compounds; zinc compounds; ferrites; nanoparticles; x-ray diffraction; thermal gravimetric analysis; differential thermal analysis; light scattering; scanning electron microscopy

  • IPEN-DOC 21598

    ICHIKAWA, RODRIGO U.; YOSHITO, WALTER K. ; SAEKI, MARGARIDA J.; MARANHAO, WILLIAN C.A. ; GOULART, FATIMA ; MARTINEZ, LUIS G. . Characterization of Mnsub(0.67)Znsub(0.33)Fesub(2)Osub(4) nanoparticles synthesized under different pH. In: INTERNATIONAL LATIN-AMERICAM CONFERENCE ON POWDER THECHNOLOGY, 10th, November 8-11, 2015, Mangaratiba, RJ. Proceedings... 2015.

    Palavras-Chave: manganese compounds; zinc compounds; ferrites; nanoparticles; x-ray diffraction; thermal gravimetric analysis; differential thermal analysis; light scattering; scanning electron microscopy

  • IPEN-DOC 19290

    GARCIA, RAFAEL H.L. ; SALIBA SILVA, ADONIS M. ; CARVALHO, ELITA F.U. ; LIMA, NELSON B. ; ICHIKAWA, RODRIGO U.; MARTINEZ, LUIZ G. . Characterization of uranium silicide powder using XRD. In: INTERNATIONAL NUCLEAR ATLANTIC CONFERENCE; MEETING ON NUCLEAR APPLICATIONS, 11th; MEETING ON REACTOR PHYSICS AND THERMAL HYDRAULICS, 18th; MEETING ON NUCLEAR INDUSTRY, 3rd, November 24-29, 2013, Recife, PE. Proceedings... Sao Paulo: ABEN, 2013, 2013.

    Palavras-Chave: uranium silicides; nuclear fuels; research reactors; materials testing reactors; quality control; x-ray diffraction; crystallography; crystal structure

  • IPEN-DOC 24817

    ICHIKAWA, RODRIGO U. ; ROCA, ALEJANDRO G.; LOPEZ-ORTEGA, ALBERTO; ESTRADER, MARTA; PERAL, INMA; TURRILLAS, XABIER; NOGUES, JOSEP. Combining X-Ray whole powder pattern modeling, rietveld and pair distribution function analyses as a novel bulk approach to study interfaces in heteronanostructures: oxidation front in FeO/Fe3O4 core/shell nanoparticles as a case study. Small, v. 14, n. 30, p. 1800804-1 - 1800804-11, 2018. DOI: 10.1002/smll.201800804

    Abstract: Understanding the microstructure in heterostructured nanoparticles is crucial to harnessing their properties. Although microscopy is ideal for this purpose, it allows for the analysis of only a few nanoparticles. Thus, there is a need for structural methods that take the whole sample into account. Here, a novel bulk‐approach based on the combined analysis of synchrotron X‐ray powder diffraction with whole powder pattern modeling, Rietveld and pair distribution function is presented. The microstructural temporal evolution of FeO/Fe3O4 core/shell nanocubes is studied at different time intervals. The results indicate that a two‐phase approach (FeO and Fe3O4) is not sufficient to successfully fit the data and two additional interface phases (FeO and Fe3O4) are needed to obtain satisfactory fits, i.e., an onion‐type structure. The analysis shows that the Fe3O4 phases grow to some extent (≈1 nm) at the expense of the FeO core. Moreover, the FeO core progressively changes its stoichiometry to accommodate more oxygen. The temporal evolution of the parameters indicates that the structure of the FeO/Fe3O4 nanocubes is rather stable, although the exact interface structure slightly evolves with time. This approach paves the way for average studies of interfaces in different kinds of heterostructured nanoparticles, particularly in cases where spectroscopic methods have some limitations.

    Palavras-Chave: iron oxides; nanoparticles; shells; oxidation; hybridization; x-ray equipment

  • IPEN-DOC 20631

    MARTINEZ, LUIS G. ; ICHIKAWA, RODRIGO U. ; IMAKUMA, KENGO ; TURRILLAS, XABIER; ORLANDO, MARCOS T.D.. Estimation of mean crystallite sizes of XRD standard reference materials produced at IPEN by XLPA. In: REUNIÃO ANUAL DE USUÁRIOS DO LABORATORIO NACIONAL DE LUZ SINCROTRON, 24., 11-12 de março, 2014, Campinas, SP. Abstract... 2014. p. 58.

    Palavras-Chave: materials; calibration standards; diffractometers; grain size; microstructure; x-ray diffraction

  • IPEN-DOC 24861

    RUBIO-MARCOS, FERNANDO; DEL CAMPO, ADOLFO; ROJAS-HERNANDEZ, ROCIO E.; RAMIREZ, MARIOLA O.; PARRA, RODRIGO; ICHIKAWA, RODRIGO U. ; RAMAJO, LEANDRO A.; BAUSA, LUISA E.; FERNANDEZ, JOSE F.. Experimental evidence of charged domain walls in lead-free ferroelectric ceramics: light-driven nanodomain switching. Nanoscale, v. 10, n. 2, p. 705-715, 2018. DOI: 10.1039/c7nr04304j

    Abstract: The control of ferroelectric domain walls at the nanometric level leads to novel interfacial properties and functionalities. In particular, the comprehension of charged domain walls, CDWs, lies at the frontier of future nanoelectronic research. Whereas many of the effects have been demonstrated for ideal archetypes, such as single crystals, and/or thin films, a similar control of CDWs on polycrystalline ferroelectrics has not been achieved. Here, we unambiguously show the presence of charged domain walls on a leadfree (K,Na)NbO3 polycrystalline system. The appearance of CDWs is observed in situ by confocal Raman microscopy and second harmonic generation microscopy. CDWs produce an internal strain gradient within each domain. Specifically, the anisotropic strain develops a crucial piece in the ferroelectric domain switching due to the coupling between the polarization of light and the ferroelectric polarization of the nanodomain in the (K,Na)NbO3 ceramic. This effect leads to the tuning of the ferroelectric domain switching by means of the light polarization angle. Our results will help to understand the relevance of charged domain walls on the ferroelectric domain switching process and may facilitate the development of domain wall nanoelectronics by remote light control utilizing polycrystalline ferroelectrics.

    Palavras-Chave: nanoelectronics; nanotechnology; ferroelectric materials; domain structure; raman spectroscopy; polycrystals

  • IPEN-DOC 25135

    ROSSETTO, CLEUSA M.; ICHIKAWA, RODRIGO U. ; MARTINEZ, LUIS G. ; CAREZZATO, GERALDO L. ; CARVALHO, ALEXANDRE M.G.; TURRILLAS, XAVIER. In situ hydration of sulfoaluminate cement mixtures monitored by synchrotron X-Ray diffraction. Materials Science Forum, v. 930, p. 153-157, 2018. DOI: 10.4028/www.scientific.net/MSF.930.153

    Abstract: Mixtures of calcium sulfoaluminate and Portland clinkers with gypsum were hydrated with deionized water. The pastes were introduced in 0.7 mm borosilicate capillary tubes and kept at 40 ºC while diffraction patterns were collected every 35 s for approximately 3 hours with a monochromatic radiation of 12 keV at the XRD1 beamline of the Laboratório Nacional de Luz Síncrotron (LNLS) in Campinas, SP - Brazil. The main crystalline phases (C2S, C3S, ettringite, ye’elemite and gypsum) involved in the hydration were quantified by Rietveld analysis. The most noticeable fact was the absence of portlandite as a crystalline precipitate, most likely due to the capture of calcium ions to form ettringite.

    Palavras-Chave: hydration; aluminates; cements; portland cement; x-ray diffraction; synchrotrons; calcium sulfates

  • IPEN-DOC 24343

    ICHIKAWA, RODRIGO U. ; LINHARES, HORACIO M.S.M.D.; PERAL, INMA; BALDOCHI, SONIA L. ; RANIERI, IZILDA M. ; TURRILLAS, XAVIER; MARTINEZ, LUIS G. . Insights into the local structure of Tb-doped KY3F10 nanoparticles from Synchrotron X‑ray Diffraction. ACS Omega, v. 02, n. 08, p. 5128-5136, 2017. DOI: 10.1021/acsomega.7b00668

    Abstract: Pure and Tb-doped nanocrystalline KY3F10 specimens were synthesized by coprecipitation, and portions of the samples underwent further heat treatment at 600 °C in a fluorinated atmosphere. Synchrotron X-ray diffraction patterns acquired at 30 keV allowed to determine both long- and shortrange ordered structures by Rietveld and pair distribution function (PDF) analyses, respectively. PDF examination of the as-synthesized sample allowed to discern a slight deviation from the basic cubic building unit because the Y−F bond lengths could be explained in S.G. I4/mmm with cell parameters a = 8.1520(9) Å and c = 11.5876(29) Å, whereas Rietveld analysis could equally well fit both the cubic and tetragonal descriptions for the heat-treated specimens. Also, PDF revealed that the as-synthesized sample exhibited less structural coherence than the heattreated one.

    Palavras-Chave: doped materials; nanoparticles; x-ray diffraction; nanocrystals; synchrotrons

  • IPEN-DOC 25450

    ICHIKAWA, RODRIGO U. . Investigação da estrutura local e média de nanopartículas por técnicas de espalhamento e difração de raios X / Local and average structure investigation of nanoparticles using X-ray scattering and diffraction methods . 2018. Tese (Doutorado em Tecnologia Nuclear) - Instituto de Pesquisas Energéticas e Nucleares - IPEN-CNEN/SP, São Paulo. 143 p. Orientador: Luis Gallego Martinez. DOI: 10.11606/T.85.2018.tde-15062018-083316

    Abstract: Neste trabalho, a estrutura local e média de nanopartículas foi estudada utilizando-se métodos de espalhamento e difração de raios X. Os métodos utilizados foram: Análise da Função de Distribuição de Pares Atômicos (Atomic Pair Distribution Function Analysis, em inglês) para o estudo do ordenamento estrutural de curto alcance, Refinamento de Rietveld e Modelamento Total do Perfil de Difração de Pó para o estudo do ordenamento médio. Os materiais estudados foram: nanopartículas de KY3F10 dopadas com Tb, nanocubos núcleo-camada (core-shell, em inglês) de FeO-Fe3O4 e nanopartículas de ferritas de Mn-Zn. O trabalho teve como objetivo demonstrar como os métodos mencionados podem ser utilizados de forma complementar para fornecer informações de curto, médio e longo alcance usando-se dados de espalhamento e difração de raios X. Neste trabalho, ressalta-se a importância de cada método no estudo da estrutura cristalina e demonstra avanço e desenvolvimento de metodologias para a sua aplicação.

    Palavras-Chave: terbium isotopes; fluorides; iron oxides; barium oxides; manganese oxides; nickel oxides; zinc oxides; ferrites; powders; crystal structure; solid state physics; interatomic forces; distribution functions; scattering; x-ray diffraction; electronic structure; nanoelectronics; charged particles; pattern recognition

  • IPEN-DOC 21758

    GOMES, LAERCIO ; LINHARES, HORACIO M. da S.M.D.; ICHIKAWA, RODRIGO U. ; MARTINEZ, LUIS G. ; BALDOCHI, SONIA L. . Luminescence properties of Yb:Er:KYsub(3)Fsub(10) nanophosphor and thermal treatment effects. Optical Materials, v. 54, p. 57-66, 2016.

    Palavras-Chave: luminescence; nanostructures; heat treatments; crystals; efficiency; excitation; spectroscopy; powders; pulses; x-ray diffraction; ytterbium; ytterbium ions; erbium; erbium ions

  • IPEN-DOC 20192

    GOMES, LAERCIO ; LINHARES, HORACIO M. da S.M.D. ; ICHIKAWA, RODRIGO U. ; MARTINEZ, LUIZ G. ; RANIERI, IZILDA M. . Luminescence properties of Yb:Nd:Tm:KYsub(3)Fsub(10) nanophosphor and thermal treatment effects. Journal of Luminescence, v. 137, p. 285-292, 2015.

    Palavras-Chave: luminescence; rare earths; nanostructures; phosphorus; energy transfer; heat treatments

  • IPEN-DOC 25151

    ICHIKAWA, RODRIGO U. ; PARRA, JOAO P.R.L.L.; MARTINS, MURILLO L.; YOSHITO, WALTER K. ; SAEKI, MARGARIDA J.; TURRILLAS, XAVIER; MARTINEZ, LUIS G. . Size-strain analysis of iron-excess Mn–Zn ferrite nanoparticles using synchrotron diffraction and its correlation with magnetic saturation and isoelectric pH. Journal of Nanoscience and Nanotechnology, v. 18, n. 8, p. 5697-5703, 2018. DOI: 10.1166/jnn.2018.15446

    Abstract: Iron-excess Mn–Zn ferrite nanoparticles were prepared by coprecipitation with sodium hydroxide (NaOH) at different concentrations (0.1, 0.2, 0.5 and 1.0 mol/L). The results of X-ray diffraction (XRD) analysis using Whole Powder Pattern Modeling (WPPM) showed that higher concentrations of NaOH promote crystallite growth and broader dispersion in crystallite sizes. Energy dispersive X-ray spectroscopy indicates that zinc loss is noticeable when [NaOH] ≥ 0.2 mol/L. XRD revealed also a significant less-crystalline phase contribution alongside the main peaks of the nanocrystalline cubic spinel ferrite phase. The less-crystalline fraction is lower for the ferrite obtained with 0.2 mol/L of NaOH, being about 50% and more than 70% for the other samples. Despite of the less-crystalline fraction and the excess of iron, no secondary phases were detected. The Warren curves showed that the concentration of NaOH significantly influences the microstrain in the crystallites, being smaller for the sample obtained with NaOH at 0.2 mol/L. The sample prepared with this condition presented the better properties to be used as magnetic tracer in clinical diagnoses combining small mean crystallite size, low microstrain, which resulted in materials with higher magnetic saturation and high surface charge under blood pH.

    Palavras-Chave: nanoparticles; ferrite; strains; fourier analysis; synchrotron radiation; x-ray diffraction

  • IPEN-DOC 24172

    DARIN, GASPAR ; IMAKUMA, KENGO ; MARTINEZ, LUIS G. ; TURRILAS, XABIER M.; ICHIKAWA, RODRIGO U. ; SILVA, ANDRE S.B. ; DURAZZO, MICHELANGELO ; RIELLA, HUMBERTO G. ; URANO, ELITA . Structural and microstructural analysis of the U-GD-O system using X-ray diffraction data. In: INTERNATIONAL NUCLEAR ATLANTIC CONFERENCE, October 22-27, 2017, Belo Horizonte, MG. Proceedings... Rio de Janeiro, RJ: Associação Brasileira de Energia Nuclear, 2017.

    Abstract: Gadolinium is one of the best neutron absorber materials and its usage can be considered as a burnable poison for Light Water Reactors (LWR) and as a sacrificial material in Sodium Fast Reactor (SFR). Most of the experiments in the literature focus on nuclear fuel with up to 12 wt% Gd2O3. Recently, the phase diagram and melting point has been investigated for high contents of Gd2O3 in the U-Gd-O system, that means a solid solution of the composition (U1-x, Gdx)O2 for 0<x<100%. In this work, we present the analysis of the U-Gd-O system for high contents of Gd2O3 using X-ray diffraction data. Rietveld analysis was applied to obtain cell parameters, atomic positions and atomic displacement factors and compared with literature avaliable. Also, the quantification of phases was performed for the different contents of Gd2O3 in the system. Finally, mean crystallite sizes were determined and correlated with the weight fraction of the phases.

    Palavras-Chave: atomic displacements; burnable poisons; critical size; gadolinium oxides; microstructure; mixtures; phase diagrams; uranium; x-ray diffraction

  • IPEN-DOC 24140

    ICHIKAWA, RODRIGO U. ; GARCIA, RAFAEL H.L. ; SILVA, ANDRE S.B. da ; TURRILLAS, XAVIER; SALIBA-SILVA, ADONIS M. ; LIMA, NELSON B. ; MARTINEZ, LUIS G. . Structural and microstructural characterization of U3Si2 nuclear fuel using X-ray diffraction. In: INTERNATIONAL NUCLEAR ATLANTIC CONFERENCE, October 22-27, 2017, Belo Horizonte, MG. Proceedings... Rio de Janeiro, RJ: Associação Brasileira de Energia Nuclear, 2017.

    Abstract: In this work, two uranium silicide powdered samples, containing 67% and 42 mol% of Si, were analyzed using X-ray diffraction (named as 67Si and 42Si). For structural characterization, Rietveld refinement was used to estimate cell parameters, volume fraction (weight percent) of crystalline phases and atomic positions. For the main phases, X-ray line profile analysis (XLPA) was used to estimate mean crystallite sizes and microstrains. The 67Si sample presents higher content of USi2 (tetragonal) and the 42Si sample presents higher content of U3Si2 (tetragonal) as identified and calculated from the XRD profiles. Overall there are no appreciable structural changes and the parameters refined are in good accordance with the ones reported in the literature. Mean crystallite sizes determined by XLPA revealed small crystallites of the order of 101 nm and low microstrain for all samples.

    Palavras-Chave: crystal structure; microstructure; nuclear fuels; powders; stoichiometry; uranium silicides

  • IPEN-DOC 22331

    ICHIKAWA, RODRIGO U. ; MARTINEZ, LUIS G. ; PEREIRA, LUIZ A.T. ; IMAKUMA, KENGO ; TURRILLAS, XABIER. Study of the microstructure in remelted zircaloy by synchrotron diffraction line profile analysis. In: REUNIÃO ANUAL DE USUÁRIOS DO LNLS, 24., 11-14 de março, 2014, Campinas, SP. Abstract... 2014. p. 61.

    Palavras-Chave: zircaloy; x-ray diffraction; size; microstructure; synchrotron radiation; strains; heat; yttrium oxides

  • IPEN-DOC 19276

    ICHIKAWA, RODRIGO U.; PEREIRA, LUIZ A.T.; IMAKUMA, KENGO ; TURRILLAS, XAVIER; MARTINEZ, LUIS G. . Study on the microstructure of recycled zircaloy by x-ray diffraction line profile analysis. In: INTERNATIONAL NUCLEAR ATLANTIC CONFERENCE; MEETING ON NUCLEAR APPLICATIONS, 11th; MEETING ON REACTOR PHYSICS AND THERMAL HYDRAULICS, 18th; MEETING ON NUCLEAR INDUSTRY, 3rd, November 24-29, 2013, Recife, PE. Proceedings... Sao Paulo: ABEN, 2013, 2013.

    Palavras-Chave: crystal defects; fuel cycle; fuel elements; heat treatments; machining; microstructure; scrap; vacuum melting; x-ray diffraction; zirconium alloys

  • IPEN-DOC 21085

    ICHIKAWA, RODRIGO U. ; LINHARES, HORACIO M.S.M.D.; TEIXEIRA, MARIA I. ; RANIERI, IZILDA M. ; TURRILLAS, XAVIER; MARTINEZ, LUIS G. . Synchrotron diffraction characterization of nanostructured KYsub(3)Fsub(10):Tb. In: INTERNATIONAL NUCLEAR ATLANTIC CONFERENCE; MEETING ON NUCLEAR APPLICATIONS, 12th; MEETING ON REACTOR PHYSICS AND THERMAL HYDRAULICS, 19th; MEETING ON NUCLEAR INDUSTRY, 4th, October 4-9, 2015, São Paulo, SP. Proceedings... 2015.

    Palavras-Chave: synchrotron radiation; x-ray diffraction; doped materials; terbium; yttrium ions; rare earths; atomic displacements; crystal structure; fluorides; nanostructures; thermoluminescence

A pesquisa no RD utiliza os recursos de busca da maioria das bases de dados. No entanto algumas dicas podem auxiliar para obter um resultado mais pertinente.

É possível efetuar a busca de um autor ou um termo em todo o RD, por meio do Buscar no Repositório , isto é, o termo solicitado será localizado em qualquer campo do RD. No entanto esse tipo de pesquisa não é recomendada a não ser que se deseje um resultado amplo e generalizado.

A pesquisa apresentará melhor resultado selecionando um dos filtros disponíveis em Navegar

Os filtros disponíveis em Navegar tais como: Coleções, Ano de publicação, Títulos, Assuntos, Autores, Revista, Tipo de publicação são autoexplicativos. O filtro, Autores IPEN apresenta uma relação com os autores vinculados ao IPEN; o ID Autor IPEN diz respeito ao número único de identificação de cada autor constante no RD e sob o qual estão agrupados todos os seus trabalhos independente das variáveis do seu nome; Tipo de acesso diz respeito à acessibilidade do documento, isto é , sujeito as leis de direitos autorais, ID RT apresenta a relação dos relatórios técnicos, restritos para consulta das comunidades indicadas.

A opção Busca avançada utiliza os conectores da lógica boleana, é o melhor recurso para combinar chaves de busca e obter documentos relevantes à sua pesquisa, utilize os filtros apresentados na caixa de seleção para refinar o resultado de busca. Pode-se adicionar vários filtros a uma mesma busca.

Exemplo:

Buscar os artigos apresentados em um evento internacional de 2015, sobre loss of coolant, do autor Maprelian.

Autor: Maprelian

Título: loss of coolant

Tipo de publicação: Texto completo de evento

Ano de publicação: 2015

Para indexação dos documentos é utilizado o Thesaurus do INIS, especializado na área nuclear e utilizado em todos os países membros da International Atomic Energy Agency – IAEA , por esse motivo, utilize os termos de busca de assunto em inglês; isto não exclui a busca livre por palavras, apenas o resultado pode não ser tão relevante ou pertinente.

95% do RD apresenta o texto completo do documento com livre acesso, para aqueles que apresentam o significa que e o documento está sujeito as leis de direitos autorais, solicita-se nesses casos contatar a Biblioteca do IPEN, bibl@ipen.br .

Ao efetuar a busca por um autor o RD apresentará uma relação de todos os trabalhos depositados no RD. No lado direito da tela são apresentados os coautores com o número de trabalhos produzidos em conjunto bem como os assuntos abordados e os respectivos anos de publicação agrupados.

O RD disponibiliza um quadro estatístico de produtividade, onde é possível visualizar o número dos trabalhos agrupados por tipo de coleção, a medida que estão sendo depositados no RD.

Na página inicial nas referências são sinalizados todos os autores IPEN, ao clicar nesse símbolo será aberta uma nova página correspondente à aquele autor – trata-se da página do pesquisador.

Na página do pesquisador, é possível verificar, as variações do nome, a relação de todos os trabalhos com texto completo bem como um quadro resumo numérico; há links para o Currículo Lattes e o Google Acadêmico ( quando esse for informado).

ATENÇÃO!

ESTE TEXTO "AJUDA" ESTÁ SUJEITO A ATUALIZAÇÕES CONSTANTES, A MEDIDA QUE NOVAS FUNCIONALIDADES E RECURSOS DE BUSCA FOREM SENDO DESENVOLVIDOS PELAS EQUIPES DA BIBLIOTECA E DA INFORMÁTICA.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

1. Portaria IPEN-CNEN/SP nº 387, que estabeleceu os princípios que nortearam a criação do RDI, clique aqui.


2. A experiência do Instituto de Pesquisas Energéticas e Nucleares (IPEN-CNEN/SP) na criação de um Repositório Digital Institucional – RDI, clique aqui.

O Repositório Digital do IPEN é um equipamento institucional de acesso aberto, criado com o objetivo de reunir, preservar, disponibilizar e conferir maior visibilidade à Produção Científica publicada pelo Instituto, desde sua criação em 1956.

Operando, inicialmente como uma base de dados referencial o Repositório foi disponibilizado na atual plataforma, em junho de 2015. No Repositório está disponível o acesso ao conteúdo digital de artigos de periódicos, eventos, nacionais e internacionais, livros, capítulos, dissertações, teses e relatórios técnicos.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.