  • IPEN-DOC 22656

    SANTOS, FELIPE A. ; SILVA, ANTONIO C. ; SANTOS, CLAUDINEI; SIMBA, BRUNO G.; BARTOLOME, JOSE F.; DURAN, TERESA; FERNANDEZ-GARCIA, ELISA; ROGERO, SIZUE O. ; MELLO-CASTANHO, SONIA R.H. . Biocide glass based on Nb2O5-SiO-CaO-Na2O system. Materials Letters, v. 183, p. 277-280, 2016. DOI: 10.1016/j.matlet.2016.07.117

    Abstract: In this work,glasses based on SiO-CaO-Na2O system containing different Nb2O5 contents were developed. Glasses were melted at 1500 °C and quenched in a metallic mould. Citotoxicity tests were performed using neutral red uptake methodology and indicated normal cell growth, which enables the use as biomaterial. Biocide activity was evaluated through glass incubation in bacterial suspension (Escherichia coli) at 37 °C under shaking. The composition with higher content of SiO2 and lower content of Nb2O5 presented higher biocide activity and the coefficient of thermal expansion indicate thermal compatibility with stainless steel 316L and titanium alloys.

    Palavras-Chave: antimicrobial agents; escherichia coli; fourier transformation; glass; infrared spectra; niobium oxides; quenching; silicon oxides; thermal expansion; x-ray diffraction


  • IPEN-DOC 07352

    ANDREOLI, M. ; LUCA, G.T.C.; SEO, E.S.M. . Characteristics of rice husks for chlorination reaction. Materials Letters, v. 44, n. 5, p. 294-298, 2000.

    Palavras-Chave: rice; pelletizing; silicon oxides; carbon; concentration ratio; stoichiometry; chlorination; grain size; impurities; physical properties; crystal structure; silicon chlorides


  • IPEN-DOC 11375

    PEREIRA, G.J.; CASTRO, R.H.R.; FLORIO, D.Z.; MUCCILLO, E.N.S. ; GOUVEA, D.. Densification and electrical conductivity of fast fired manganese-doped ceria ceramics. Materials Letters, v. 59, n. 10, p. 1195-1199, 2005.

    Palavras-Chave: manganese; doped materials; cerium oxides; ceramics; electric conductivity; impedance; spectroscopy


  • IPEN-DOC 10229

    LIMA, L.F.C.P. ; GODOY, A.L.E. ; MUCCILLO, E.N.S. . Elastic modulus of porous Ce-TZP ceramics. Materials Letters, v. 58, n. 1-2, p. 172-175, 2004.

    Palavras-Chave: ceramics; porosity; tetragonal zirconia polycrystals; cerium; doped materials; elasticity; dynamic mechanical analysis


  • IPEN-DOC 20267

    SILVA, MAVIAEL J. da ; MOYA, JOSE S.; PECHARROMAN, CARLOS; SANZ, JESUS; MELLO CASTANHO, SONIA . High barium content lead and alkaline-free glasses. Materials Letters, v. 136, p. 345-348, 2014.

    Palavras-Chave: barium oxides; lead; glass; refraction; refractive index; nmr spectra; nuclear magnetic resonance; spectroscopy


  • IPEN-DOC 22606

    MUCCILLO, R. ; CERRI, J.A.; LEITE, E.R.; LONGO, E.; VARELA, J.A.. Impedance spectroscopy of SnO2: CoO during sintering. Materials Letters, v. 30, n. 1, p. 125-130, 1997. DOI: 10.1016/S0167-577X(97)80001-8

    Abstract: SnO2 : m mol% Co0 (0.5 <= m <= 6.0) ceramic specimens were studied by impedance spectroscopy in the 5 Hz-13 MHz frequency range during heating cold-pressed specimens from room temperature to 1250°C. The electrical resistivity during sintering decreases from 4 to 6 orders of magnitude in the 400-1.500 K temperature range depending on the amount of COO. An increase in electrical resistivity in the 570-670 K range is related to the release of adsorbed water. The results for the 970-1500 K show that the higher the amount of the Co0 addition, the lower is the temperature at which SnO, : Co0 reaches a minimum electrical rlzsistivity. This suggests that oxygen point defects created by dissolution of cobalt ions in the SnO, lattice are controlling the densification rate of these ceramics.

    Palavras-Chave: tin oxides; cobalt oxides; electric conductivity; spectroscopy; dilatometry; sintering; ceramics; doped materials; impedance; materials testing


  • IPEN-DOC 09281

    MUCCILLO, E.N.S. ; AVILA, D.M. . Impedance spectroscopy of tetragonal zirconia polycrystals doped with ceria. Materials Letters, v. 56, n. 4, p. 454-459, 2002.

    Palavras-Chave: zirconium oxides; polycrystals; cerium oxides; powders; milling; mixing; coprecipitation; comparative evaluations; microstructure; electric conductivity; solid electrolytes; impedance; spectroscopy


  • IPEN-DOC 07730

    COSENTINO, I.C. ; MUCCILLO, R. . Lattice parameters of thoria-yttria solid solutions. Materials Letters, v. 48, n. 5, p. 253-257, 2001.

    Palavras-Chave: solid electrolytes; solid solutions; ceramics; thorium oxides; yttrium oxides; powders; sintering; lattice parameters


  • IPEN-DOC 14728

    SERNA, M.M. ; ROSSI, J.L. . MC complex carbide in AISI M2 high-speed steel. Materials Letters, v. 63, n. 8, p. 691-693, 2009.

    Palavras-Chave: carbides; steels; x-ray diffraction; powder metallurgy; microstructure; sprays; mechanical properties


  • IPEN-DOC 17745

    MOYA, J.S.; CABAL, B.; SANZ, J.; SILVA, A.C. da; MELLO CASTANHO, S. ; TORRECILLAS, R.; ROJO, F.. Mechanism of calcium lixiviation in soda-lime glasses with a strong biocide activity. Materials Letters, v. 70, p. 113-115, 2012.

    Palavras-Chave: silicon oxides; sodium oxides; calcium oxides; boron oxides; leaching; bacteria; disinfectants; escherichia coli; nuclear magnetic resonance; spectroscopy


  • IPEN-DOC 15549

    JAIMES, RUTH F.V.V.; AFONSO, MONICA L.C. de A.; ROGERO, SIZUE O. ; AGOSTINHO, SILVIA M.L.; BARBOSA, CELSO A.. New material for orthopedic implants: electrochemical study of nickel free P558 stainless steel in minimum essential medium. Materials Letters, v. 64, n. 13, p. 1476-1479, 2010.

    Palavras-Chave: prostheses; stainless steels; nickel; electrochemistry


  • IPEN-DOC 25143

    SOUZA, J.P. ; GROSSO, R.L. ; MUCCILLO, R. ; MUCCILLO, E.N.S. . Phase composition and ionic conductivity of zirconia stabilized with scandia and europia. Materials Letters, v. 229, p. 53-56, 2018. DOI: 10.1016/j.matlet.2018.06.091

    Abstract: Sintered specimens of zirconia-10 mol% scandia pure and codoped (up to 1.25 mol%) with europium sexquioxide were prepared by solid-state synthesis, aiming to stabilize at room temperature the high-conductivity cubic phase. High-temperature X-ray diffraction and differential scanning calorimetry results reveal that small amounts of the codopant reduce the enthalpy of phase transition, and full stabilization is evidenced for 1 mol% europium sexquioxide. The low-temperature (<600 C) ionic conductivity increases with increasing codopant content.

    Palavras-Chave: zirconium; sintering; solid electrolytes; phase transformations; scandium; europium; thermal analysis; electrical properties; ionic conductivity


  • IPEN-DOC 09282

    MUCCILLO, E.N.S. ; ROCHA, R.A.; MUCCILLO, R. . Preparation of Gdsub(2)Osub(3) - doped ZrOsub(2) by polymeric precursor techniques. Materials Letters, v. 53, n. 4/5, p. 353-358, 2002.

    Palavras-Chave: solid electrolytes; gadolinium oxides; zirconium oxides; solid solutions; chemical preparation; citrates; pva; gels; powders; thermal analysis; microstructure; particle size; comparative evaluations


  • IPEN-DOC 13026

    SPINACE, ESTEVAM V. ; FARIAS, LUCIANA A.; LINARDI, MARCELO ; OLIVEIRA NETO, ALMIR . Preparation of Pt/Sn/C and PtSnNi/C electrocatalysts using the alcohol-reduction process. Materials Letters, v. 62, p. 2099-2102, 2008.

    Palavras-Chave: alcohol fuel cells; reduction; ethanol fuels; electrocatalysts; platinum; tin; carbon; nickel


  • IPEN-DOC 14920

    COSENTINO, I.C. ; MUCCILLO, R. . Properties of thoria-yttria solid electrolytes prepared by the citrate technique. Materials Letters, v. 32, n. 5-6, p. 295-300, 1997.

    Palavras-Chave: microstructure; sintering; solid electrolytes; thorium oxides; powder metallurgy; impedance


  • IPEN-DOC 06098

    MUCCILLO, R. ; SAITO, N.H.; MUCCILLO, E.N.S. . Properties of zirconia-magnesia solid electrolytes prepared by the citrate method. Materials Letters, v. 25, p. 165-169, 1995.

    Palavras-Chave: powders; zirconium oxides; magnesium oxides; citrates; solid electrolytes


  • IPEN-DOC 25968

    GROSSO, ROBSON L. ; MUCHE, DERECK N.F.; YONAMINE, TAEKO; MUCCILLO, ELIANA N.S. ; DILLON, SHEN J.; CASTRO, RICARDO H.R.. Sintering of translucent and single-phase nanostructured scandia-stabilized zirconia. Materials Letters, v. 253, p. 246-249, 2019. DOI: 10.1016/j.matlet.2019.06.076

    Abstract: Fully-dense and single-phase nanostructured scandia-stabilized zirconia specimens were produced by high-pressure spark plasma sintering technique. Nanocrystalline powders were prepared by the coprecipitation method. Green pellets were sintered at temperatures varying from 700 to 900 C and pressures from 1.4 to 2 GPa, resulting in dense microstructures with single-phase fluorite-type cubic structure within a wide range of Sc2O3 content (6–15 mol%). The average grain size of sintered specimens ranged from 8 to 20 nm. Transmittance spectra confirm translucence in sintered specimens, which is consistent with full density. The results reported here reveal that the polymorphism challenge in the zirconiascandia system can be successfully suppressed by this consolidation technique, which allows for controlling the grain size of bulk specimens.

    Palavras-Chave: zirconium oxides; sintering; nanostructures; microstructure; ceramics; grain size; scandium; stabilization


  • IPEN-DOC 20188

    GROSSO, R.L. ; MUCCILLO, R. ; MUCCILLO, E.N.S. . Stabilization of the cubic phase in zirconia-scandia by niobium oxidfe addition. Materials Letters, v. 134, p. 27-29, 2014.

    Palavras-Chave: zirconium oxides; scandium oxides; niobium oxides; stabilization; thermodynamic properties; phase transformations; electron microscopy; nanostructures; particles; x-ray diffraction


  • IPEN-DOC 21333

    AFONSO, MONICA L.C. de A.; JAIMES, RUTH F.V.V.; NASCENTE, PEDRO A.P.; ROGERO, SIZUE O. ; AGOSTINHO, SILVIA M.L.. Surface characterization, electrochemical behaviour and cytotoxicity of UNS S31254 stainless steel for orthopaedic applications. Materials Letters, v. 148, p. 71-75, 2015.

    Palavras-Chave: stainless steels; sodium chlorides; implants; surfaces; electrochemistry; toxicity; polarimetry; amperometry; spectroscopy; x-ray photoelectron spectroscopy; comparative evaluations


  • IPEN-DOC 07136

    MUCCILLO, R. ; BUISSA NETTO, R.C.; MUCCILLO, E.N.S. . Synthesis and characterization of calcia fully stabilized zirconia solid electrolytes. Materials Letters, v. 49, n. 3/4, p. 197-201, 2001.

    Palavras-Chave: ceramics; powders; synthesis; zirconium oxides; calcium oxides; citrates; solid solutions; solid electrolytes; microstructure; electric conductivity


A pesquisa no RD utiliza os recursos de busca da maioria das bases de dados. No entanto algumas dicas podem auxiliar para obter um resultado mais pertinente.

É possível efetuar a busca de um autor ou um termo em todo o RD, por meio do Buscar no Repositório , isto é, o termo solicitado será localizado em qualquer campo do RD. No entanto esse tipo de pesquisa não é recomendada a não ser que se deseje um resultado amplo e generalizado.

A pesquisa apresentará melhor resultado selecionando um dos filtros disponíveis em Navegar

Os filtros disponíveis em Navegar tais como: Coleções, Ano de publicação, Títulos, Assuntos, Autores, Revista, Tipo de publicação são autoexplicativos. O filtro, Autores IPEN apresenta uma relação com os autores vinculados ao IPEN; o ID Autor IPEN diz respeito ao número único de identificação de cada autor constante no RD e sob o qual estão agrupados todos os seus trabalhos independente das variáveis do seu nome; Tipo de acesso diz respeito à acessibilidade do documento, isto é , sujeito as leis de direitos autorais, ID RT apresenta a relação dos relatórios técnicos, restritos para consulta das comunidades indicadas.

A opção Busca avançada utiliza os conectores da lógica boleana, é o melhor recurso para combinar chaves de busca e obter documentos relevantes à sua pesquisa, utilize os filtros apresentados na caixa de seleção para refinar o resultado de busca. Pode-se adicionar vários filtros a uma mesma busca.


Buscar os artigos apresentados em um evento internacional de 2015, sobre loss of coolant, do autor Maprelian.

Autor: Maprelian

Título: loss of coolant

Tipo de publicação: Texto completo de evento

Ano de publicação: 2015

Para indexação dos documentos é utilizado o Thesaurus do INIS, especializado na área nuclear e utilizado em todos os países membros da International Atomic Energy Agency – IAEA , por esse motivo, utilize os termos de busca de assunto em inglês; isto não exclui a busca livre por palavras, apenas o resultado pode não ser tão relevante ou pertinente.

95% do RD apresenta o texto completo do documento com livre acesso, para aqueles que apresentam o significa que e o documento está sujeito as leis de direitos autorais, solicita-se nesses casos contatar a Biblioteca do IPEN, .

Ao efetuar a busca por um autor o RD apresentará uma relação de todos os trabalhos depositados no RD. No lado direito da tela são apresentados os coautores com o número de trabalhos produzidos em conjunto bem como os assuntos abordados e os respectivos anos de publicação agrupados.

O RD disponibiliza um quadro estatístico de produtividade, onde é possível visualizar o número dos trabalhos agrupados por tipo de coleção, a medida que estão sendo depositados no RD.

Na página inicial nas referências são sinalizados todos os autores IPEN, ao clicar nesse símbolo será aberta uma nova página correspondente à aquele autor – trata-se da página do pesquisador.

Na página do pesquisador, é possível verificar, as variações do nome, a relação de todos os trabalhos com texto completo bem como um quadro resumo numérico; há links para o Currículo Lattes e o Google Acadêmico ( quando esse for informado).



O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

1. Portaria IPEN-CNEN/SP nº 387, que estabeleceu os princípios que nortearam a criação do RDI, clique aqui.

2. A experiência do Instituto de Pesquisas Energéticas e Nucleares (IPEN-CNEN/SP) na criação de um Repositório Digital Institucional – RDI, clique aqui.