Pitting susceptibility of AISI 304 stainless steel after cold rolling
Carregando...
Data
Data de publicação:
2014
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
É parte de
CONGRESSO BRASILEIRO DE CORROSÃO, 34.; INTERNATIONAL CORROSION MEETING, 5th.; CONGRESO IBEROAMERICANO DE CORROSIÓN Y PROTECCIÓN, 10th.; CONCURSO DE FOTOGRAFIA DE CORROSÃO E DEGRADAÇÃO DE MATERIAIS, 19.; EXPOSIÇÃO DE TECNOLOGIAS PARA PREVENÇÃO E CONTROLE DA CORROSÃO, 34
Exportar
Resumo
The austenitic grade AISI 304 stainless steel is traditionally employed for processing
equipment in chemical plants due to its relatively good corrosion resistance and mechanical
stability. However, it is susceptible to pitting corrosion due to chloride attack which can lead
to catastrophic failures during operation. Cold rolling of the metallic sheets used to construct
equipment such as tanks and pressure vessels can further aggravate the situation by increasing
the material’s susceptibility to localized corrosion. In this work the pitting corrosion
resistance of cold rolled AISI 304 stainless steel plates was assessed using
chronoamperometric curves and potentiodynamic polarization curves. Cold rolling was
performed in a two-roll mill at room temperature, achieving thickness reductions ranging
from 10% to 70%. The presence of pits on the surface of the samples was assessed using
optical microscopy. The onset of pitting corrosion was closely related to the strain level of the
rolled plates. There was a steep decrease of resistance to localized attack as the thickness
reduction increased.
Como referenciar
CORREA, OLANDIR V.; OLIVEIRA, MARA C.L. de; ANTUNES, RENATO A. Pitting susceptibility of AISI 304 stainless steel after cold rolling. In: CONGRESSO BRASILEIRO DE CORROSÃO, 34.; INTERNATIONAL CORROSION MEETING, 5th.; CONGRESO IBEROAMERICANO DE CORROSIÓN Y PROTECCIÓN, 10th.; CONCURSO DE FOTOGRAFIA DE CORROSÃO E DEGRADAÇÃO DE MATERIAIS, 19.; EXPOSIÇÃO DE TECNOLOGIAS PARA PREVENÇÃO E CONTROLE DA CORROSÃO, 34, 19-23 de maio, 2014, Fortaleza, CE. Anais... Rio de Janeiro, RJ: Associação Brasileira de Corrosão – ABRACO, 2014. Disponível em: http://repositorio.ipen.br/handle/123456789/26436. Acesso em: 27 Feb 2025.