On the microstructure characterization of the AA2098-T351 alloy welded by FSW

Carregando...
Imagem de Miniatura
Data
2018
Data de publicação:
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
Materials Characterization
Exportar
Mendeley
Projetos de Pesquisa
Unidades Organizacionais
Fascículo
Resumo
The complex structure of the AA2098-T351 alloy welded by friction stir welding (FSW) was investigated by transmission electron microscopy (TEM), differential scanning calorimetry (DSC) and microhardness measurements. Thermal modelling process of the FSW process was carried out by soldering thermocouples at distances of 6, 9 and 12 mm from the weld centerline, and thermocouple measurements were used as input data into the model. Finite element software COMSOL v5.2 was used for data analysis. The prevailing phases in the base metal (BM) are T1 (Al2CuLi) theta' (Al2Cu), delta'/beta'(Al-3(Li,Zr)) and Omega (Al2Cu). In the heat affected zone (HAZ), either in the retreating or advancing sides, theta' phase was not identified. In the thermomechanical affected zone (TMAZ), T1, delta'/beta', GP zones phase were detected in the retreating side, whereas T1 and Guinier-Preston (GP) zones were not observed in the advancing side. This result supports the asymmetric behavior observed in the microhardness profile of the weld. In the stir zone (SZ), GP zones, T1, delta'/beta' (Al-3(Li,Zr)) and Omega were identified.

Como referenciar
MILAGRE, MARIANA X.; MOGILI, NAGA V.; DONATUS, UYIME; GIORJAO, RAFAEL A.R.; TERADA, MAYSA; ARAUJO, JOAO V.S.; MACHADO, CARULINE S.C.; COSTA, ISOLDA. On the microstructure characterization of the AA2098-T351 alloy welded by FSW. Materials Characterization, v. 140, p. 233-246, 2018. DOI: 10.1016/j.matchar.2018.04.015. Disponível em: http://repositorio.ipen.br/handle/123456789/28972. Acesso em: 28 Mar 2024.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.

Agência de fomento
Coleções