Heat treatments effects on nickel-based superalloy inconel 713C
Carregando...
Data
2019
Data de publicação:
Autores IPEN
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
Metals
Exportar
Resumo
The purpose of this work is to study the effect of heat treatments on the microstructure of
the nickel-based superalloy Inconel 713C. Three different conditions were studied and the results
compared: (1) as cast; (2) solid solution treatment (1179 C/2 h) and (3) stabilization heat treatment
(1179 C/2 h plus 926 C/16 h). Inconel 713C is normally used in the as-cast condition, an
improvement in the 980 C stress-rupture life is often obtained by a solution heat treatment. However,
the material in this condition tested under high stress at 730 C shows a marked decreased in rupture
life and ductility. The mechanical resistance in creep increases in Inconel 713C by precipitation
hardening phase, with
’ (Ni3Al) formed during the heat treatments. The characterization techniques
used were: chemical analysis, hardness testing, X-ray diffraction, optical microscopy and scanning
electron microscopy (SEM), EDS analyzes and thermocalculation. The SEM and EDS analysis
illustrated the
,
’ and carbides. The matrix phase (
), has in its constitution the precipitation
of the
’ phase, in a cubic form, and in some regions, carbides were modified through the heat
treatments. (M23C6-type) and boride (M3B2 type) identified with the use of the thermocalculation.
The heat treatments increase the relative intensity of niobium in the carbides. The hardness test was
not achieved because the material was overaged.