Synthesis and characterization of bioactive ceramic in CaO-MgO-SiO2 system

Carregando...
Imagem de Miniatura
Data
Data de publicação:
2018
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
É parte de
INTERNATIONAL CONGRESS ON CERAMICS, 7th; CONGRESSO BRASILEIRO DE CERÂMICA, 62.
Exportar
Mendeley
Projetos de Pesquisa
Unidades Organizacionais
Fascículo
Resumo
Na2SiO3 solution and chloride solutions of calcium and magnesium were used as raw materials. HCl was added to Na2SiO3 solution resulting in gel of silica. In order to obtain a mixture of Si gel, Ca2+ and Mg2+, calcium and magnesium solutions were blended into the gel. After adding NaOH to the mixture, Ca2+ and Mg2+ ions precipitated as hydroxides. Subsequently, it was dried to attain the ceramic precursor powder, which was calcined at 900 ºC for 1h, compacted into a pellet form and sintered at 1200 ºC for 2h. The ceramic body was characterized by SEM, XRD and FTIR. In vitro test for bioactivity verification was performed in SBF. A surface deposition of hydroxyapatite on the ceramic body was observed after 3 days. The cytotoxicity test revealed that the material has cell viability above 70%, meaning that it is not toxic for the cells, according to ISO 10993-5 standard.

Como referenciar
LEME, D.R.; MORAIS, V.R.; RODAS, A.C.D.; HIGA, O.Z.; YAMAGATA, C. Synthesis and characterization of bioactive ceramic in CaO-MgO-SiO2 system. In: INTERNATIONAL CONGRESS ON CERAMICS, 7th; CONGRESSO BRASILEIRO DE CERÂMICA, 62., June 17-21, 2018, Foz do Iguaçu, PR. Proceedings... p. 36-45. Disponível em: http://repositorio.ipen.br/handle/123456789/29681. Acesso em: 29 Mar 2024.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.

Agência de fomento
Coleções