  • IPEN-DOC 22769

    COSTENARO, HELLEN; QUEIROZ, FERNANDA M.; TERADA, MAYSA; MARIE-GEORGES, OLIVIER; COSTA, ISOLDA ; MELO, HERCILIO G. de. Corrosion protection of AA2524-T3 anodized in tartaric-sulfuric acid bath and protected with hybrid sol-gel coating. Key Engineering Materials, v. 710, p. 210-215, 2016. DOI: 10.4028/www.scientific.net/KEM.710.210

    Abstract: 2xxx Al alloys are particularly sensitive to localized corrosion in chloride environments and in order to maintain their integrity, minimize maintenance needs and repairs, and to maximize component life, protective treatments are required. Anodizing is an electrochemical process based on the growth of the Al oxide layer by applying anodic potentials. One of the alternatives is tartaric/sulphuric acid (TSA) anodizing, which is environmentally compliant and provides corrosion resistance properties, compatible with the requirements of the aerospace industry with appropriate paint adhesion. In this study, AA2524-T3 specimens were anodized in a tartaric-sulfuric acid bath (TSA) and subsequently protected by application of a hybrid sol–gel coating. The sol–gel coating was prepared using a solution with high water content (58 %v/v) and obtained by the hydrolysis and condensation of tetraethoxysilane (TEOS) and 3-glycidoxypropyltrimethoxysilane (GPTMS). The corrosion resistance evaluation of both unsealed and coated samples was carried out in a sodium chloride solution by EIS as a function of immersion time. The results were also fitted using electrical equivalent circuits.

    Palavras-Chave: corrosion protection; tartaric acid; sulfuric acid; sol-gel process; alloys; corrosion; coatings; anodization

    Icon

  • IPEN-DOC 25752

    TERADA, M. ; QUEIROZ, F.M.; AGUIAR, D.B.S.; AYUSSO, V.H. ; COSTENARO, H.; OLIVIER, M.G.; MELO, H.G. de; COSTA, I. . Corrosion resistance of tartaric-sulfuric acid anodized AA2024-T3 sealed with Ce and protected with hybrid sol–gel coating. Surface & Coatings Technology, v. 372, p. 422-426, 2019. DOI: 10.1016/j.surfcoat.2019.05.028

    Abstract: 2024 aluminum alloys are widely used in the aerospace industry due to properties as lightweight, high specific strength and durability. However, they are prone to localized corrosion due to its high amount of intermetallics. A promising method to protect the exposed metal surface is to use eco-friendly alternative corrosion inhibitors in combination with a barrier coating system. In this study, a treatment in an aqueous solution with the addition of cerium ions has been proposed and its effects on the corrosion resistance of the AA2024-T3 alloy were investigated. Samples were anodized, hydrothermally treated in aqueous solutions, containing or not cerium ions at the boiling temperature and then coated with sol-gel. The effect of Ce ions in the characteristics of the surface film formed, such as morphology and corrosion resistance, was investigated by scanning electron microscopy and electrochemical impedance spectroscopy (EIS). The EIS results showed that the addition of Ce(III) ions improved the corrosion resistance of the AA 2024-T3 TSA anodized and hydrothermally treated.

    Palavras-Chave: aluminium alloys; corrosion; anodization; tartaric acid; sulfuric acid; cerium ions; sol-gel process; electrochemistry

    Icon

  • IPEN-DOC 26654

    TERADA, MAYSA ; QUEIROZ, FERNANDA M.; COSTENARO, HELEN; AYUSSO, VICTOR H. ; OLIVIER, MARJORIE; COSTA, ISOLDA ; MELO, HERCILIO G. de. Effect of cerium addition to a hydrothermal treatment on the corrosion protection of the tartaric-sulfuric acid anodized AA2524-T3. Corrosion, v. 75, n. 9, p. 1110-1117, 2019. DOI: 10.5006/3063

    Abstract: To protect Al alloys from corrosion, standard procedures in the aerospace industry use chromium-based acid anodizing with subsequent post-treatment steps also containing hexavalent chromium (Cr(VI)) ions. However, environmental and health related concerns associated with Cr(VI) have encouraged the search for new surface treatments providing effective corrosion protection without the drawback of generating toxic residues. In this investigation, a hydrothermal treatment in aqueous solution with cerium ions is proposed as a post-treatment for tartaric-sulfuric acid (TSA) anodizing, and its effects on the AA2524-T3 alloy corrosion resistance investigated. The effect of Ce on the characteristics of the surface film formed, such as morphology and corrosion resistance, is investigated by scanning electron microscopy and electrochemical impedance spectroscopy (EIS). The results show that the hydrothermal treatment in solution containing Ce(III) ions presents a less stable behavior than the treatment in boiling water. However, the results of the EIS experiments show recovery of the protective properties of the system, indicating that some self-healing properties must be imparted to the system.

    Palavras-Chave: cerium; corrosion protection; hydrothermal systems; tartaric acid; sulfuric acid; aluminium alloys; corrosion fatigue; scanning electron microscopy

    Icon

  • IPEN-DOC 23560

    QUEIROZ, F.M. ; BUGARIN, A.F.S. ; HAMMEL, N.P. ; CAPELOSSI, V.R.; TERADA, M.; COSTA, I. . EIS behavior of anodized and primer coated AA2198–T851 compared to AA2024–T3 exposed to salt spray CASS test. Surface and Interface Analysis, v. 48, n. 8, p. 755-766, 2016. DOI: 10.1002/sia.5982

    Abstract: In this investigation, the corrosion behavior of AA2198–T851 was compared to AA2024–T3 by electrochemical impedance spectroscopy and the surface of both alloys was analyzed by Field Emission Gun (FEG) scanning electron microscopy (SEM) and Xray energy dispersive analysis (EDX). Electrochemical impedance spectroscopy (EIS) results for the uncoated surface of both alloys showed higher pitting susceptibility associated to the AA2198–T851 alloy comparatively to the AA2024–T3. In order to improve the corrosion resistance of both alloys, tartaric sulphuric acid anodising (TSA) was carried out with both alloys followed by primer application. The corrosion resistance of the anodized and primer coated samples was also evaluated by CASS salt spray test followed by EIS tests at increasing periods of exposure to the CASS test. The results showed larger amounts of corrosion products associated to the primer coated AA2198–T851 alloy comparatively to the AA2024–T3 alloy. Diffusionwas only indicated in the EIS results of the AA2198–T851 samples likely because of large amounts of porous corrosion products on the exposed surface of this alloy to the corrosive environment.

    Palavras-Chave: aluminium alloys; electrochemistry; impedance; spectroscopy; tartaric acid; sulfuric acid; corrosion; corrosion resistance; corrosion products; anodes; layers

    Icon

  • IPEN-DOC 25862

    RAMIREZ, OSCAR M.P.; QUEIROZ, FERNANDA M.; TERADA, MAYSA; DONATUS, UYIME ; COSTA, ISOLDA ; OLIVIER, MARIE-GEORGES; MELO, HERCILIO G. de. EIS investigation of a Ce‐based posttreatment step on the corrosion behaviour of Alclad AA2024 anodized in TSA. Surface and Interface Analysis, v. 51, n. 12, SI, p. 1260-1275, 2019. DOI: 10.1002/sia.6633

    Abstract: In the aircraft industry, anodizing and posttreatment steps use Cr (VI) compounds, which, despite offering good corrosion resistance and self‐healing properties, are highly toxic and carcinogenic. Ce compounds are recognized as efficient corrosion inhibitors for Al alloys, and several works report self‐healing ability for these chemicals. In this investigation, the corrosion resistance of Alclad AA2024‐T3 alloy anodized in tartaric‐sulphuric acid (TSA) bath and posttreated in a solution comprising cerium nitrate without and with hydrogen peroxide was evaluated. The purpose is to investigate the potentiality of using hydrothermal treatment in Ce nitrate solution as candidate to replace Cr (VI) posttreatment. The aim is to provide a posttreatment step which, while improving the corrosion resistance, does not plug the mouths of the pores maintaining the adhesion properties of the porous anodic layer. Microstructural characterization was carried out by SEM‐EDS whereas corrosion resistance was evaluated by EIS. The surface analysis showed that the posttreatments, all performed at 50°C, kept the open structure of the pores. EIS analysis showed that the posttreatments performed in the H2O2 solution for short immersion times were the most effective in improving the corrosion resistance of the samples, whereas electrical equivalent circuit (EEC) fitting of the data indicated sealing of the porous layer during the immersion of the different samples in the test solution. SEM‐EDS analysis of the samples posttreated in the H2O2 containing solution, prior and after the corrosion test, showed the presence of Ce oxy‐hydroxide randomly deposited on the sample surface, indicating that Ce could be incorporated/stored in the anodic layer.

    Palavras-Chave: aluminium alloys; anodization; cerium nitrates; equivalent circuits; impedance; spectroscopy; electrochemical cells; corrosion resistance; tartaric acid; sulfuric acid

    Icon

  • IPEN-DOC 27388

    ALI, BAKHAT; STEFANI, HELIO A.; IMRAN, MUHAMMAD; IRFAN, AHMAD; ASSIRI, MOHAMMED A.; FELINTO, MARIA C.F.C. ; KHALID, MUHAMMAD; AL-SEHEMI, ABDULLAH G.. Synthesis, structure study, first-principles investigations and luminescence properties of europium and terbium complexes. Journal of Fluorescence, v. 30, n. 6, p. 1345-1355, 2020. DOI: 10.1007/s10895-020-02613-z

    Abstract: The synthesis of 1-benzyl-2-((2-Aminoethyl) amino)-5-oxopyrrolidine-3,4-diyl diacetate (boad), an oxopyrrolidine type ligand; designed to coordinate lanthanides (Eu3+ and Tb3+) to get luminescent material. The target complexes showed good photoluminescence properties, which indicate that this type of compound can be used as sensitizers having luminescence for the green (Tb3+) and red (Eu3+) emission. The obtained results revealed that sensitizer efficiency can be improved by adding ligands like acac (Eu(acac)3, which has also enhanced the luminescence quantum output and period for Eu3+ ions. The ground state geometries were developed by using density functional theory at B3LYP/6-31G** level. The charge transfer analysis and electronic properties were performed. The Europium and Terbium complexes formation with boad ligand was explored based on molecular electrostatic potential, MDC-q charges, and frontier molecular orbitals (FMOs) analysis.

    Palavras-Chave: synthesis; europium complexes; terbium complexes; luminescence; tartaric acid; pyrrolidines; rare earths; photoluminescence; density functional method; nmr spectra

    Icon

A pesquisa no RD utiliza os recursos de busca da maioria das bases de dados. No entanto algumas dicas podem auxiliar para obter um resultado mais pertinente.

É possível efetuar a busca de um autor ou um termo em todo o RD, por meio do Buscar no Repositório , isto é, o termo solicitado será localizado em qualquer campo do RD. No entanto esse tipo de pesquisa não é recomendada a não ser que se deseje um resultado amplo e generalizado.

A pesquisa apresentará melhor resultado selecionando um dos filtros disponíveis em Navegar

Os filtros disponíveis em Navegar tais como: Coleções, Ano de publicação, Títulos, Assuntos, Autores, Revista, Tipo de publicação são autoexplicativos. O filtro, Autores IPEN apresenta uma relação com os autores vinculados ao IPEN; o ID Autor IPEN diz respeito ao número único de identificação de cada autor constante no RD e sob o qual estão agrupados todos os seus trabalhos independente das variáveis do seu nome; Tipo de acesso diz respeito à acessibilidade do documento, isto é , sujeito as leis de direitos autorais, ID RT apresenta a relação dos relatórios técnicos, restritos para consulta das comunidades indicadas.

A opção Busca avançada utiliza os conectores da lógica boleana, é o melhor recurso para combinar chaves de busca e obter documentos relevantes à sua pesquisa, utilize os filtros apresentados na caixa de seleção para refinar o resultado de busca. Pode-se adicionar vários filtros a uma mesma busca.

Exemplo:

Buscar os artigos apresentados em um evento internacional de 2015, sobre loss of coolant, do autor Maprelian.

Autor: Maprelian

Título: loss of coolant

Tipo de publicação: Texto completo de evento

Ano de publicação: 2015

Para indexação dos documentos é utilizado o Thesaurus do INIS, especializado na área nuclear e utilizado em todos os países membros da International Atomic Energy Agency – IAEA , por esse motivo, utilize os termos de busca de assunto em inglês; isto não exclui a busca livre por palavras, apenas o resultado pode não ser tão relevante ou pertinente.

95% do RD apresenta o texto completo do documento com livre acesso, para aqueles que apresentam o significa que e o documento está sujeito as leis de direitos autorais, solicita-se nesses casos contatar a Biblioteca do IPEN, bibl@ipen.br .

Ao efetuar a busca por um autor o RD apresentará uma relação de todos os trabalhos depositados no RD. No lado direito da tela são apresentados os coautores com o número de trabalhos produzidos em conjunto bem como os assuntos abordados e os respectivos anos de publicação agrupados.

O RD disponibiliza um quadro estatístico de produtividade, onde é possível visualizar o número dos trabalhos agrupados por tipo de coleção, a medida que estão sendo depositados no RD.

Na página inicial nas referências são sinalizados todos os autores IPEN, ao clicar nesse símbolo será aberta uma nova página correspondente à aquele autor – trata-se da página do pesquisador.

Na página do pesquisador, é possível verificar, as variações do nome, a relação de todos os trabalhos com texto completo bem como um quadro resumo numérico; há links para o Currículo Lattes e o Google Acadêmico ( quando esse for informado).

ATENÇÃO!

ESTE TEXTO "AJUDA" ESTÁ SUJEITO A ATUALIZAÇÕES CONSTANTES, A MEDIDA QUE NOVAS FUNCIONALIDADES E RECURSOS DE BUSCA FOREM SENDO DESENVOLVIDOS PELAS EQUIPES DA BIBLIOTECA E DA INFORMÁTICA.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

1. Portaria IPEN-CNEN/SP nº 387, que estabeleceu os princípios que nortearam a criação do RDI, clique aqui.


2. A experiência do Instituto de Pesquisas Energéticas e Nucleares (IPEN-CNEN/SP) na criação de um Repositório Digital Institucional – RDI, clique aqui.