  • IPEN-DOC 23652

    HARADA, JULIO ; MACEDO, JOSE R.N.; MACHADO, GLAUSON A.F. ; VALENZUELA-DIAZ, FRANCISCO; MOURA, ESPERIDIANA A.B. ; ROSA, DERVAL S.. Effects of carbon black incorporation on morphological, mechanical and thermal properties of biodegradable films. In: IKHMAYIES, SHADIA J. (Ed.); LI, BOWEN (Ed.); CARPENTER, JOHN S. (Ed.); HWANG, JIANN-YANG (Ed.); MONTEIRO, SERGIO N. (Ed.); LI, JIAN (Ed.); FIRRAO, DONATO (Ed.); ZHANG, MINGMING (Ed.); PENG, ZHIWEI (Ed.); ESCOBEDO-DIAZ, JUAN P. (Ed.); BAI, CHENGUANG (Ed.) TMS ANNUAL MEETING & EXHIBITION, 145th; CHARACTERIZATION OF MINERALS, METALS, AND MATERIALS, February 14-18, 2016, Nashville, Tennessee, USA. Proceedings... Hoboken, New Jersey: John Wiley & Sons, Inc., 2016. p. 697-704.

    Abstract: This work evaluates the effects of carbon black incorporation on morphological, mechanical and thermal properties of biodegradable films. The biodegradable composite films based on PBAT/PLA blend and PBAT/PLA blend containing 2 wt. % of carbon black were prepared by me lt extrusion, using a twin screw extruder machine and blown extrusion process. The properties of biodegradable film samples were investigated by tensile tests, XRD, MFI, TGA, DSC and FE-SEM analysis and the correlation between properties was discussed.

    Icon

  • IPEN-DOC 23651

    GONZALEZ-RUIZ, JESUS; YATACO-LAZARO, LOURDES; VIRGINIO, SUELI ; SILVA-VALENZUELA, MARIA das G. da; MOURA, ESPERIDIANA ; VALENZUELA-DIAZ, FRANCISCO. Effects of graphene oxide addition on mechanical and thermal properties of evoh films. In: IKHMAYIES, SHADIA J. (Ed.); LI, BOWEN (Ed.); CARPENTER, JOHN S. (Ed.); HWANG, JIANN-YANG (Ed.); MONTEIRO, SERGIO N. (Ed.); LI, JIAN (Ed.); FIRRAO, DONATO (Ed.); ZHANG, MINGMING (Ed.); PENG, ZHIWEI (Ed.); ESCOBEDO-DIAZ, JUAN P. (Ed.); BAI, CHENGUANG (Ed.) TMS ANNUAL MEETING & EXHIBITION, 145th; CHARACTERIZATION OF MINERALS, METALS, AND MATERIALS, February 14-18, 2016, Nashville, Tennessee, USA. Proceedings... Hoboken, New Jersey: John Wiley & Sons, Inc., 2016. p. 667-674.

    Abstract: Currently, ethylene vinyl alcohol (EVOH) is one of the oxygen barrier materials most used for food packaging. The addition of graphene oxide nanosheets to the EVOH matrix is employed to improve their mechanical and barrier properties. In this work, films of EVOH- based composites reinforced with graphene oxide were prepared by melt extrusion, using a twin screw extruder machine and blown extrusion process. The graphene oxide was prepared via chemical oxidation of natural graphite and then was exfoliated into nanosheets using the sonochemical method. The composite films samples were characterized using FTIR and DSC analysis. In addition, their mechanical properties were also determined.

    Icon

  • IPEN-DOC 20811

    MACHADO, MESSIAS dos S.; GODOY, RENATO B. ; SILVA, ANDRESSA ; LIMA, ROBERTA; OLIVEIRA, RENE R.; VALENZUELA-DIAZ, FRANCISCO; MOURA, ESPERIDIANA . influence of clay exfoliation on the properties of evoh/clay flexible fims. In: CARPENTER, JOHN S. (Ed.); BAI, CHENGUANG (Ed.); ESCOBEDO, JUAN P. (Ed.); HWANG, JIANN-YANG (Ed.); LKHMAYIES, SHADIA (Ed.); LI, BOWEN (Ed.); LI, JIAN (Ed.); MONTEIRO, SERGIO N. (Ed.); PENG, ZHIWEI (Ed.); ZHANG, MINGMING (Ed.) CHARACTERIZATION OF MINERALS, METALS, AND MATERIALS. 144th . ANNUAL MEETING & EXIBITION, March 15-19, 2015, Orlando, Florida. Proceedings... New York: Wiley , 2015, 2015. p. 273-279.

    Palavras-Chave: copolymers; ethylene; vinyl acetate; alcohols; clays; films; flexibility; tensile properties; x-ray diffraction; calorimetry

    Icon

  • IPEN-DOC 22626

    ORTIZ, ANGEL ; AKBULUT, MESHUDE; SANTANA, JULYANA G. ; RANGARI, VIJAY K.; VALENZUELA-DIAZ, FRANCISCO; GUVEN, OLGUN; MOURA, ESPERIDIANA . Morphology, optical transparency and oxygen barrier of EVOH/graphene oxide films. In: BRAZILIAN CONFERENCE ON COMPOSITE MATERIALS, 3rd, August 28-31, 2016, Gramado, RS. Proceedings... 2016.

    Abstract: Food packaging materials require high gas and moisture barrier in other to preserve the quality of the products during storage and handling. Polyolefin materials have been widely used due to their water vapor resistance. Ethylene–vinyl alcohol copolymer (EVOH) is used as a gas barrier layer in packaging products that require high gas barrier. However, EVOH is very sensitive to moisture and its gas barrier ability deteriorates in high relative humidity conditions. In order to overcome the adverse effects of moisture on EVOH film this paper studies the incorporation of small amount of graphene oxide in EVOH by melt processing and evaluates their effects on morphology, optical transparency and oxygen barrier of EVOH film. The EVOH/Graphene oxide (EVOH/GO) film were processed by twin-screw extrusion and extrusion blown film processing. The films was characterized by XRD, FEG-SEM, and UV/VIS analysis. In addition, the oxygen transmission rate (OTR) were performed at 23 C, 0 % and 90 % relative humidity using an OX-TRAN (MOCON Inc.). According to the results of the optical transparency measured, the EVOH/GO retaining good transparency films for all graphene oxide percentage added. The graphene oxide at only 0.1 wt. % into the EVOH matrix drastically improved the oxygen barrier properties of EVOH/GO flexible film in both, 0 % and 90 % of the relative humidity test conditions.

    Icon

  • IPEN-DOC 20805

    ROCHA GOMES, LEILA V. de; FERMINO, DANILO; MOURA, ESPERIDIANA ; VALENZUELA, MARIA das G.; VALENZUELA-DIAZ, FRANCISCO. Polypropylene nanocomposites reinforced with organophilic clay and brazilian nut fibers. In: CARPENTER, JOHN S. (Ed.); BAI, CHENGUANG (Ed.); HWANG, JIANN-YANG (Ed.); LKHMAYIES, SHADIA (Ed.); LI, BOWEN (Ed.); MONTEIRO, SERGIO N. (Ed.); PENG, ZHIWEI (Ed.); ZHANG, MINGMING (Ed.) CHARACTERIZATION OF MINERALS, METALS, AND MATERIALS. 143rd . ANNUAL MEETING & EXIBITION, February 16-20, 2014, San Diego, California. Proceedings... New York: Wiley , 2014, 2014. p. 89-96.

    Palavras-Chave: polypropylene; nanostructures; composite materials; reinforced materials; clays; brazil; nuts; fibers; mechanical properties; x-ray diffraction; optical microscopy; scanning electron microscopy

    Icon

  • IPEN-DOC 22627

    BARREIRA, DAILI A.S ; SANTANA, JULYANA G. ; LAZARO, LOURDES Y.; RUIZ, JESUS G.; VALENZUELA-DIAZ, FRANCISCO; GUVEN, OLGUN; MOURA, ESPERIDIANA A.B. . Preparation of EVOH/graphene oxide by blown film extrusion – correlation between film properties and graphene oxide addition. In: BRAZILIAN CONFERENCE ON COMPOSITE MATERIALS, 3rd, August 28-31, 2016, Gramado, RS. Proceedings... 2016.

    Abstract: This study reports the preparation of EVOH films reinforced with graphene oxide by twin-screw extrusion and blown film extrusion processing. The preparation of EVOH/Graphene oxide (EVOH/GO) films was carried out in two steps: EVOH with Graphene oxide powder (0-0.5 wt. %) was fed into a co-rotating twin-screw extruder, then the EVOH/GO nanocomposite was transformed into thin films using an extrusion blown film, single screw machine with 25 mm diameter and specimens test samples were obtained. The purpose of this study was to evaluate the correlation between mechanical properties and thermal stability of EVOH/GO films and the amount of graphene oxide added to the EVOH matrix. Tensile tests were conducted using an INSTRON Testing Machine. DSC and TG analysis were used for investigate the thermal stability of EVOH/Graphene oxide films. DSC analysis results showed that melting temperature (Tm), melting enthalpy (Hm) and consequently the degree of crystallinity (Xc) of neat EVOH increased with the incorporation of the 0.1 and 0.5 wt. % of GO. TG of the composites showed a great difference in weight loss and in the onset degradation temperature when compared with the neat EVOH. The more important change was observed for EVOH/GO with 0.2 wt. % GO content that presented an increase of the onset degradation temperature. A significant enhancement of the tensile strength at break of EVOH/GO flexible film without important effects on the elongation at break were also observed, except for EVOH/GO with 0.2 wt. % GO content that presented an important increase in both, tensile strength and elongation at break. It can be concluded that the addition of GO is an effective means to improve the EVOH flexible films properties and led to the obtaining of packaging materials with superior properties suitable for several industrial applications.

    Icon

A pesquisa no RD utiliza os recursos de busca da maioria das bases de dados. No entanto algumas dicas podem auxiliar para obter um resultado mais pertinente.

É possível efetuar a busca de um autor ou um termo em todo o RD, por meio do Buscar no Repositório , isto é, o termo solicitado será localizado em qualquer campo do RD. No entanto esse tipo de pesquisa não é recomendada a não ser que se deseje um resultado amplo e generalizado.

A pesquisa apresentará melhor resultado selecionando um dos filtros disponíveis em Navegar

Os filtros disponíveis em Navegar tais como: Coleções, Ano de publicação, Títulos, Assuntos, Autores, Revista, Tipo de publicação são autoexplicativos. O filtro, Autores IPEN apresenta uma relação com os autores vinculados ao IPEN; o ID Autor IPEN diz respeito ao número único de identificação de cada autor constante no RD e sob o qual estão agrupados todos os seus trabalhos independente das variáveis do seu nome; Tipo de acesso diz respeito à acessibilidade do documento, isto é , sujeito as leis de direitos autorais, ID RT apresenta a relação dos relatórios técnicos, restritos para consulta das comunidades indicadas.

A opção Busca avançada utiliza os conectores da lógica boleana, é o melhor recurso para combinar chaves de busca e obter documentos relevantes à sua pesquisa, utilize os filtros apresentados na caixa de seleção para refinar o resultado de busca. Pode-se adicionar vários filtros a uma mesma busca.

Exemplo:

Buscar os artigos apresentados em um evento internacional de 2015, sobre loss of coolant, do autor Maprelian.

Autor: Maprelian

Título: loss of coolant

Tipo de publicação: Texto completo de evento

Ano de publicação: 2015

Para indexação dos documentos é utilizado o Thesaurus do INIS, especializado na área nuclear e utilizado em todos os países membros da International Atomic Energy Agency – IAEA , por esse motivo, utilize os termos de busca de assunto em inglês; isto não exclui a busca livre por palavras, apenas o resultado pode não ser tão relevante ou pertinente.

95% do RD apresenta o texto completo do documento com livre acesso, para aqueles que apresentam o significa que e o documento está sujeito as leis de direitos autorais, solicita-se nesses casos contatar a Biblioteca do IPEN, bibl@ipen.br .

Ao efetuar a busca por um autor o RD apresentará uma relação de todos os trabalhos depositados no RD. No lado direito da tela são apresentados os coautores com o número de trabalhos produzidos em conjunto bem como os assuntos abordados e os respectivos anos de publicação agrupados.

O RD disponibiliza um quadro estatístico de produtividade, onde é possível visualizar o número dos trabalhos agrupados por tipo de coleção, a medida que estão sendo depositados no RD.

Na página inicial nas referências são sinalizados todos os autores IPEN, ao clicar nesse símbolo será aberta uma nova página correspondente à aquele autor – trata-se da página do pesquisador.

Na página do pesquisador, é possível verificar, as variações do nome, a relação de todos os trabalhos com texto completo bem como um quadro resumo numérico; há links para o Currículo Lattes e o Google Acadêmico ( quando esse for informado).

ATENÇÃO!

ESTE TEXTO "AJUDA" ESTÁ SUJEITO A ATUALIZAÇÕES CONSTANTES, A MEDIDA QUE NOVAS FUNCIONALIDADES E RECURSOS DE BUSCA FOREM SENDO DESENVOLVIDOS PELAS EQUIPES DA BIBLIOTECA E DA INFORMÁTICA.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

1. Portaria IPEN-CNEN/SP nº 387, que estabeleceu os princípios que nortearam a criação do RDI, clique aqui.


2. A experiência do Instituto de Pesquisas Energéticas e Nucleares (IPEN-CNEN/SP) na criação de um Repositório Digital Institucional – RDI, clique aqui.