OLANDIR VERCINO CORREA
7 resultados
Resultados de Busca
Agora exibindo 1 - 7 de 7
Artigo IPEN-doc 25006 Characterization and photocatalytic behavior of TiO2 thin films grown by MOCVD process2017 - BENTO, RODRIGO T.; OLIVEIRA, EDUARDO C. de; SZURKALO, MARGARIDA; CORREA, OLANDIR V.; PILLIS, MARINA F.This research aims to evaluate the influence of the thickness on the photocatalytic behavior of TiO2 thin films grown at 400ºC by metalorganic chemical vapor deposition. Titanium dioxide films with 280 and 468 nm of thickness were grown on borosilicate substrates. The photocatalytic behavior was evaluated by monitoring the degradation of methyl orange dye under UV light for 2h. The results show that both films presented anatase crystalline phase and that increasing the thickness the grain size and the roughness were also increased. The best photocatalytic performance was attributed to the film of 468 nm of thickness that exhibited 40% of dye degradation after 2h under UV light.Artigo IPEN-doc 22413 High temperature oxidation behavior of yttrium dioxide coated Fe-20Cr alloy2016 - PILLIS, MARINA F.; CORREA, OLANDIR V.; RAMANATHAN, LALGUDI V.Resumo IPEN-doc 15877 Resistência a oxidação de um aço comercial recoberto por um filme de Cr2O3 por meio da técnica de deposição química em fase vapor2010 - PILLIS, M.F.; GALEGO, M.; SERNA, M.M.; CORREA, O.V.; RAMANATHAN, L.V.Este trabalho teve por objetivo estudar o comportamento de oxidação do aço AISI 1020 sem e com revestimento de um filme nanoestruturado de Cr2O3. O revestimento foi obtido por meio da técnica de deposição química em fase vapor. O precursor utilizado foi o acetil‐acetonato de cromo. Foi utilizado ainda gás oxigênio para permitir a formação de Cr2O3. Os crescimentos foram conduzidos sob pressão de 2 mbar, à temperatura de 600°C por 30 minutos. Os testes de oxidação foram realizados ao ar em balança termogravimétrica a 800 e 1000ºC por 20h. As amostras assim obtidas foram caracterizadas por meio de técnicas de microscopia eletrônica de varredura com emissão de campo, análises químicas por energia dispersiva, e difração de raios X.Resumo IPEN-doc 19754 Nanostructured coatings to protect metallic materials at high temperatures2013 - FERNANDES, S.M.C.; PILLIS, M.F.; CUNHA, C.A.; CORREA, O.V.; RAMANATHAN, L.V.Artigo IPEN-doc 12588 Estudo do comportamento de oxidação de ligas DeCr e FeCrY recobertas por uma tinta a abase de aluminio2006 - PILLIS, M.F.; CORREA, O.V.; ARAUJO, E.G. de; RAMANATHAN, L.V.Artigo IPEN-doc 18560 Resistência à oxidação do aço-carbono SAE 1020 recoberto por um filme de Crsub(2)Osub(3)2012 - PILLIS, MARIANA F.; CORREA, OLANDIR V.; RAMANATHAN, LALGUDI V.Artigo IPEN-doc 15997 Resistência à oxidação da liga Fe20Cr revestida com Ysub(2)Osub(3)2008 - PILLIS, MARINA F.; ARAUJO, EDVAL G. de; CORREA, OLANDIR V.; RAMANATHAN, LALGUDI V.Neste trabalho está apresentado o efeito do revestimento de Y2O3 sobre o comportamento de oxidação da liga Fe20Cr. Foram efetuados ensaios isotérmicos de até 200h a 1000°C ao ar. O comportamento de oxidação foi avaliado por meio do ganho de massa por unidade de área em função do tempo de oxidação. As curvas de oxidação mostraram que a adição superficial de Y2O3 reduziu sensivelmente o ganho de massa da liga para períodos prolongados de tempo. Análises via EDS realizadas na secção transversal da amostra revestida indicaram a existência de uma camada rica em cromo próximo à interface metal/óxido. Numa região próxima à interface revestimento/gás as análises indicaram a presença dos elementos Y e Cr, sugerindo ter havido difusão de Cr através da camada de Y2O3. As análises por DRX sugeriram a existência das fases Y2O3 e YCrO3. Observou-se macroscopicamente que o pó de Y2O3 aplicado sobre a superfície tinha inicialmente coloração branca, e que após os testes de oxidação o revestimento tornava-se esverdeado. Estas observações corroboram a difusão de Cr do substrato para a camada de revestimento, através do reticulado do Y2O3.