FALCON, J.M.OTUBO, L.AOKI, I.V.2017-01-182017-01-182016FALCON, J.M.; OTUBO, L.; AOKI, I.V. Highly ordered mesoporous silica loaded with dodecylamine for smart anticorrosion coatings. <b>Surface & Coatings Technology</b>, v. 303, p. 319-329, 2016. DOI: <a href="https://dx.doi.org/10.1016/j.surfcoat.2015.11.029">10.1016/j.surfcoat.2015.11.029</a>. Disponível em: http://repositorio.ipen.br/handle/123456789/26994.0257-8972http://repositorio.ipen.br/handle/123456789/26994The development of nanoscience and technology has devoted significant attention to studies on hollowparticles. Among these materials, mesoporous silica nanoparticles have recently attracted attention as potential nanocontainers due to their high stability, biocompatibility, large surface area, controllable pore diameter and easy surface functionalization.Mesoporous silica nanoparticles can uptake, store and release organic or inorganic molecules of various sizes, shapes and functionalities. The aimof thiswork is to study the use ofmesoporous silica with hexagonally ordered (4–14 nm) for active corrosion protection of carbon steel.Mesoporous silicawas characterized by X-ray diffraction (XRD), nitrogen adsorption isotherms, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Mesoporous silica structures were loaded with dodecylamine and embedded into an alkyd primer with a weight load ratio of 15 wt.% of mesoporous silica. Kinetics of the release of inhibitor was evaluated by electrochemical impedance measurements in aerated 0.1 mol/L NaCl solution containing 1 wt.% of mesoporous silica at different pH values (2.0, 6.2 and 9.0). The anticorrosive performance of carbon steel coatedwith alkyd primer loadedwith 15wt.% ofmesoporous silica with entrapped dodecylamine was demonstrated by electrochemical impedance spectroscopy (EIS) and scanning vibrating electrode technique (SVET). Kinetics of inhibitor releasing curves showed that for pH 2.0 condition the release of inhibitor was faster in comparison to other pH conditions (9.0 and 6.2) showing that this complex porous system provides high loading capacity and efficient inhibitor release in lowpH. In addition, due to the release of inhibitor during the corrosion process,well-pronounced active anticorrosion properties and self-healing were provided and confirmed by EIS and SVET measurements. Coated sampleswere also evaluated in a salt spray chamber and the self-healing effect was also remarkable.319-329openAccesssilicacontainersnanoparticlescoatingscorrosion inhibitorsaminescorrosion protectioncarbon steelsx-ray diffractionscanning electron microscopytransmission electron microscopyArtigo de periódico30310.1016/j.surfcoat.2015.11.029https://orcid.org/0000-0002-6078-229X76.43