FIM, R.G.T.SILVA, M.R.M.SILVA, S.C.CASINI, J.C.S.WENDHAUSEN, P.A.P.TAKIISHI, H.2019-08-232019-08-232018FIM, R.G.T.; SILVA, M.R.M.; SILVA, S.C.; CASINI, J.C.S.; WENDHAUSEN, P.A.P.; TAKIISHI, H. Influence of milling time on magnetic properties and microstructure of sintered Nd-Fe-B based permanent magnets. <b>Materials Science Forum</b>, v. 930, p. 445-448, 2018. DOI: <a href="https://dx.doi.org/10.4028/www.scientific.net/MSF.930.445">10.4028/www.scientific.net/MSF.930.445</a>. Disponível em: http://repositorio.ipen.br/handle/123456789/30120.0255-5476http://repositorio.ipen.br/handle/123456789/30120In this paper, the effect of the grain size on sintered Nd-Fe-B based permanent magnets was investigated. In order, the magnets were produced by different milling times at 200 rpm and then vacuum sintered at 1373 K for 60 minutes followed by cooling outside the furnace. The magnets either produced by lower and higher milling times (30 and 75 minutes) exhibited lower remanence and coercivity, due the inhomogeneous distribution of the grain sizes. The magnet produced by intermediary milling time (45 minutes) exhibited the highest properties among all samples, with remanence of 1.06 T, coercivity of 891.3 KA.m-1, maximum energy product of 211 KJ.m3 and a squareness factor equal 0.92.445-448openAccessneodymiummagnetspermanent magnetsmicrostructuremillingmagnetic propertiesdemagnetizationArtigo de periódico93010.4028/www.scientific.net/MSF.930.445Sem Percentil15.50