QUEIROZ, FERNANDA M.BUGARIN, ALINE de F.S.AYUSSO, VICTOR H.TERADA, MAYSACOSTA, ISOLDA2023-12-012023-12-012023QUEIROZ, FERNANDA M.; BUGARIN, ALINE de F.S.; AYUSSO, VICTOR H.; TERADA, MAYSA; COSTA, ISOLDA. Investigation on the Effect of a Chromium-Free Sealing Treatment for the Corrosion Resistance of AA2198-T851 after Tartaric Sulphuric Anodizing (TSA). <b>Corrosion and Materials Degradation</b>, v. 4, n. 2, p. 331-344, 2023. DOI: <a href="https://dx.doi.org/10.3390/cmd4020017">10.3390/cmd4020017</a>. Disponível em: http://repositorio.ipen.br/handle/123456789/34225.2624-5558http://repositorio.ipen.br/handle/123456789/34225The AA 2198-T851 is a third-generation Al-Li alloy developed for use in the aircraft industry. Al-Li alloys are susceptible to localized corrosion due to their complex microstructure resulting from the used thermomechanical treatment. In order to prevent localized corrosion, these alloys are usually protected by anodizing in order to avoid a corrosive environment. Subsequently, for anodizing, a sealing treatment is usually performed for parts. Some sealing treatments use hexavalent-chromiumion-containing solutions. In this investigation, a chromium-free sealing treatment in a solution with cerium ions has been carried out, and the effect on the corrosion resistance of the AA2198-T851 alloy was investigated. Hydrothermally sealed or unsealed samples were also tested for corrosion resistance for comparison reasons. The corrosion resistance of the anodized aluminum alloy, either hydrothermally sealed or in a cerium-ion-containing solution, was evaluated in a sodium chloride solution by electrochemical impedance spectroscopy as a function of immersion time. The samples sealed in a cerium-containing solution increased their corrosion resistance when compared to the hydrothermally sealed. The effectiveness of the sealing process with cerium that was observed in the electrochemical tests indicated that after the corrosive attack of the barrier layer, there was a “sealing” process of the sample surface.331-344openAccesscorrosion resistancetartaric acidsulfuric acidanodizationcerium ionsArtigo de periódico2410.3390/cmd40200170000-0002-4987-3334https://orcid.org/0000-0002-4987-3334Sem PercentilSem Percentil CiteScore