MARIANA XAVIER MILAGRE
3 resultados
Resultados de Busca
Agora exibindo 1 - 3 de 3
Artigo IPEN-doc 28770 TSA anodising voltage effects on the near-surface coarse intermetallic particles in the AA2024-T3 and AA2198-T8 alloys2022 - ARAUJO, JOAO V. de S.; MILAGRE, MARIANA X.; KLUMPP, RAFAEL E.; AYUSSO, VICTOR H.; DONATUS, UYIME; COSTA, ISOLDAIn this study, the behaviour of the micrometric particles of the AA2198-T8 alloy during anodising at various voltages and the effect of anodising voltage on the anodised surface morphology have been investigated in a tartaric-sulfuric acid anodising solution. The results were compared with that of the AA2024-T3 alloy. For the AA2198-T8 alloy, partial dissolution of these particles occurred at 0, 3 and 4 V. Besides, for potentials above 5 V, there is a preferential dissolution of the intermetallic particles. For the AA2024-T3 alloy, the results indicated a total dissolution of the micrometric particles at 0 V and a partial dissolution at 3 V, whereas above 4 V total dissolution occurred. Between 1 and 2 V, no dissolution was observed for both alloys. The preferential dissolution of the micrometric particles resulted in defects in the anodic film and cavities on the anodised surfaces.Artigo IPEN-doc 25861 Effect of surface treatments on the localized corrosion resistance of the AA2198‐T8 aluminum lithium alloy welded by FSW process2019 - MACHADO, CARULINE de S.C.; KLUMPP, RAFAEL E.; AYUSSO, VICTOR H.; DONATUS, UYIME; MILAGRE, MARIANA X.; ARAUJO, JOAO V. de S.; MACHADO, GLAUSON A.F.; COSTA, ISOLDAIn this work, the effect of eight types of surface treatments on the corrosion resistance of friction stir welded samples of an AA2198‐T8 Al‐Cu‐Li alloy were tested and compared in an attempt to find suitable alternatives to toxic and carcinogenic hexavalent chromium treatments. All the samples were anodized and subjected to different post‐anodizing treatments. The post‐anodizing treatments were (1) hydrothermal treatment in Ce (NO3)3 6H2O solution; (2) hydrothermal treatment in Ce (NO3)3 6H2O solution with H2O2; (3) hydrothermal treatment in boiling water; (4) hexavalent chromium conversion coating; and (5) immersion in BTSE (bis‐1,2‐(triethoxysilyl) ethane. The corrosion resistance of the treated samples was evaluated by immersion tests in sodium chloride solution (0.1 mol L−1 NaCl) and electrochemical impedance spectroscopy (EIS) of the friction stir weldment. The results showed that among the alternative treatments, the Ce‐containing solutions presented the best corrosion resistance, especially when used without peroxide.Artigo IPEN-doc 25535 Influência da composição da solução de tratamento de superfície na resistência à corrosão da liga AA2024-T32019 - KLUMPP, RAFAEL E.; SILVA, REJANE M.P. da; DONATUS, UYIME; MACHADO, CARULINE de S.C.; AYUSSO, VICTOR H.; MILAGRE, MARIANA X.; ARAUJO, JOAO V. de S.; COSTA, ISOLDAOs tratamentos de superfície de ligas de alumínio em soluções contendo íons de terras raras têm se mostrado promissores para a substituição dos tratamentos que utilizam íons de cromo hexavalente em sua composição. A composição das soluções de tratamento com terras raras é um fator importante na propriedade de proteção à corrosão da camada superficial formada. Neste trabalho, o efeito da adição de peróxido de hidrogênio à solução de tratamento para proteção à corrosão da liga AA2024-T3 foi investigado por técnicas eletroquímicas e microscópicas. Os resultados mostraram que a adição do peróxido de hidrogênio altera a morfologia da camada, o mecanismo de formação desta e resulta em propriedades de proteção levemente inferiores às da camada formada na ausência de peróxido.