MARIANA XAVIER MILAGRE
3 resultados
Resultados de Busca
Agora exibindo 1 - 3 de 3
Artigo IPEN-doc 28531 Influence of chloride ions concentration on the development of severe localised corrosion and its effects on the electrochemical response of the 2198-T8 alloy2021 - MACHADO, CARULINE de S.C.; SILVA, REJANE M.P. da; ARAUJO, JOAO V. de S.; MILAGRE, MARIANA X.; DONATUS, UYIME; VIVEIROS, BARBARA V.G. de; KLUMPP, RAFAEL E.; COSTA, ISOLDAThe development of severe localised corrosion (SLC) on the 2198-T8 alloy was investigated in solutions of various NaCl concentrations (0.001, 0.005 and 0.01 mol L−1). Immersion tests, optical profilometry, conventional and local electrochemical analyses were performed to evaluate the corrosion behaviour of the alloy. Immersion tests showed that the alloy is susceptible to SLC in all conditions, although the pits sizes were dependent on the solution concentration. The largest anodic areas, corresponding to SLC sites, were observed for the sample immersed in 0.001 mol L−1 NaCl, whereas pits with similar sizes were observed for the samples immersed in solutions with 0.005 and 0.01 mol L−1 of NaCl. Moreover, the maximum depth of attack was observed for the sample immersed in 0.001 mol L−1 NaCl. These results were in agreement with the scanning ionselective electrode technique (SIET) maps which showed stronger acidification on the sample exposed to 0.001 mol L−1 NaCl solution.Artigo IPEN-doc 25861 Effect of surface treatments on the localized corrosion resistance of the AA2198‐T8 aluminum lithium alloy welded by FSW process2019 - MACHADO, CARULINE de S.C.; KLUMPP, RAFAEL E.; AYUSSO, VICTOR H.; DONATUS, UYIME; MILAGRE, MARIANA X.; ARAUJO, JOAO V. de S.; MACHADO, GLAUSON A.F.; COSTA, ISOLDAIn this work, the effect of eight types of surface treatments on the corrosion resistance of friction stir welded samples of an AA2198‐T8 Al‐Cu‐Li alloy were tested and compared in an attempt to find suitable alternatives to toxic and carcinogenic hexavalent chromium treatments. All the samples were anodized and subjected to different post‐anodizing treatments. The post‐anodizing treatments were (1) hydrothermal treatment in Ce (NO3)3 6H2O solution; (2) hydrothermal treatment in Ce (NO3)3 6H2O solution with H2O2; (3) hydrothermal treatment in boiling water; (4) hexavalent chromium conversion coating; and (5) immersion in BTSE (bis‐1,2‐(triethoxysilyl) ethane. The corrosion resistance of the treated samples was evaluated by immersion tests in sodium chloride solution (0.1 mol L−1 NaCl) and electrochemical impedance spectroscopy (EIS) of the friction stir weldment. The results showed that among the alternative treatments, the Ce‐containing solutions presented the best corrosion resistance, especially when used without peroxide.Artigo IPEN-doc 25834 The effect of surface pretreatment on the corrosion behaviour of silanated AA2198‐T851 Al‐Cu‐Li alloy2019 - DONATUS, UYIME; KLUMPP, RAFAEL E.; MOGILI, NAGA V.V.; ANTUNES, RENATO A.; MILAGRE, MARIANA X.; COSTA, ISOLDAThe corrosion behaviour of silanated AA2198‐T851 alloy substrates with and with no manufacturing‐process induced near‐surface deformed layer (MPI‐NSDL) has been investigated. Two methods (alkaline etching + desmutting and mechanical polishing) were employed in removing the MPI‐NSDL. Silanization was performed using 2‐bistriethoxysilylethane. Electrochemical impedance spectroscopy (EIS), salt spray test, and microscopy techniques were employed in the investigation of the corrosion behaviours. The studies revealed that polishing appeared to be the best silanating pre‐treatment (compared with degreasing and etching + desmutting) for the new generation AA2198‐T851 Al‐Cu‐Li alloy, and this was reflected in the EIS spectra. The etched + desmutted and the degreased surface with MPI‐NSDL did not respond well to silanization and presented more pitting sites per square millimeter. However, the severity of corrosion per pit was more on the polished sample compared with the other two. Also, the corrosion mechanisms were different for the three cases.