Strontium and cobalt doped-lanthanum chromite
2015 - SETZ, L.F.G.; SANTACRUZ, I.; LEON-REINA, L.; TORRE, A.G. De la; ARANDA, M.A.G.; MELLO CASTANHO, S.R.H.; MORENO, R.; COLOMER, M.T.
Perovskite powders prepared by combustion synthesis with a nominal composition of La0.800Sr0.200Cr0.920Co0.080O3.000 δ were obtained from the corresponding metal nitrates, and characterised in terms of in-situ phase development (crystalline structure and thermal behaviour). Synchrotron X-ray powder diffraction (SXRPD) and Rietveld analyses demonstrated that the as-prepared powder showed an orthorhombic perovskite structure with an estimated composition of La0.803Sr0.197Cr0.966Co0.034O3.000 δ. Second phases present in the as-prepared powder were m-LaCrO4, CoLa1.250Sr0.750O4.000, c-CoCr2.000O4.000 and m-SrCrO4.000. Sintering processes, including phase transition (from orthorhombic to rhombohedral) of the main phase and, melting/evaporation of second phases have been studied by DTA/TGA and dilatometric studies; the results were in full agreement with those detected by High-Temperature Synchrotron X-ray powder diffraction (HT-SXRPD). The transition temperature was determined to be 1380 1C by dilatometric studies, and between 1240 and 1405 1C by HT-SXRPD. Dye-pressed samples sintered at 1600 1C/4 h showed a density of 98.9 dth%. The phase transition is an irreversible process since the sintered perovskite, measured at room temperature after cooling, only showed the rhombohedral phase as main phase. The evaluation of the linearity of the conductivity versus the inverse of temperature and the activation energy values of the sintered material indicated that the electrical conduction occurs via the non-adiabatic small-polaron mechanism in either air or hydrogen atmosphere. In the reducing environment, the perovskite shows significantly reduced electrical conductivity compared with that in air, as it is expected for a p-type conductor. & 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Rheological study of doped lanthanum chromite aqueous suspension
2011 - SETZ, L.F.G.; SANTACRUZ, I.; COLOMER, M.T.; MORENO, R.; MELLO CASTANHO, S.R.H.
Comportamento reologico de suspensoes aquosas de cromito de lantanio - colagem em moldes de gesso (slip casting)
2008 - SETZ, L.F.G.; SANTACRUZ, I.; COLOMER, M.T.; MORENO, R.; MELLO CASTANHO, S.R.H.
Analise reologica de suspensoes aquosas de cromito de lantanio
2008 - SETZ, L.F.G.; SANTACRUZ, I.; COLOMER, M.T.; MORENO, R.; MELLO CASTANHO, S.R.H.
Processamento e conformacao de fitas (tape casting) a partir de suspensoes coloidais de cromito de lantanio sintetizado por reacao de combustao
2009 - SETZ, L.F.G.; MELLO CASTANHO, S.R.H.; SANTACRUZ, I.; COLOMER, M.T.; MORENO, R.
Physicochemical characterization of strontium and cobalt-doped lanthanum chromite powders produced by combustion synthesis
2009 - SETZ, LUIZ F.G.; MELLO CASTANHO, SONIA R.H.; MORENO, RODRIGO; COLOMER, MARIA T.
Tape casting of strontium and cobalt doped lanthanum chromite suspensions
2010 - SETZ, LUIZ F.G.; SANTACRUZ, ISABEL; COLOMER, M.T.; MELLO CASTANHO, SONIA R.H.; MORENO, RODRIGO
Fabrication of Sr- and Co-doped lanthanum chromite interconnectors for SOFC
2011 - SETZ, L.F.G.; SANTACRUZ, I.; COLOMER, M.T.; MELLO CASTANHO, S.R.H.; MORENO, R.
Comportamento reológico de suspensões aquosas de cromito de lantânio
2011 - SETZ, L.F.G.; SANTACRUZ, I.; COLOMER, M.T.; MORENO, R.; MELLO CASTANHO, S.R.H.
Influencia da atmosfera na sinterização do cromito de lantânio dopado
2013 - SETZ, L.F.G.; MELLO CASTANHO, S.R.H.; SANTACRUZ, I.; MORENO, R.; COLOMER, M.T.
O cromito de lantânio (LaCrO3 ) para ser utilizado como interconector em células a combustível de óxido sólido, ademais de possuir condutividade elétrica adequada, deve apresentar alta densidade, contribuindo com a estanqueidade dos gases utilizados. Utilizando LaCrO3 dopado com Sr e Co sintetizado por combustão, estudou-se o efeito das atmosferas inerte (argônio) e oxidante (ar) no comportamento de sinterização e densificação. As peças foram sinterizadas em dilatômetro, caracterizadas com difração de raios X e as densidades foram determinadas pelo método de Arquimedes. Na observação das microestruturas formadas utilizou-se microscopia eletrônica de varredura. Os resultados mostram que as duas atmosferas favorecem a densificação do cromito de lantânio dopado; porém, ciclos térmicos em meios oxidantes podem prejudicar o desempenho do material quando em utilização como interconector.