LILIAN NINOSHA MURIEL BRAGUIN
3 resultados
Resultados de Busca
Agora exibindo 1 - 3 de 3
Artigo IPEN-doc 28361 A study on corrosion resistance of ISO 5832-1 austenitic stainless steel used as orthopedic implant2020 - BRAGUIN, L.N.M.; SILVA, C.A.J. da; BERBEL, L.O.; VIVEIROS, B.V.G. de; ROSSI, J.L.; COSTA, I.; SAIKI, M.The ISO 5832-1 austenitic stainless steel used as biomaterial is largely applied in the area of orthopedics, especially in the manufacture of implants, such as temporary or permanent replacement of bone structures. The objective of this study was to evaluate the localized corrosion resistance of the ISO 5832-1 stainless steel used in orthopedic implants by electrochemical tests in two different solutions. The results of this study are of great interest to evaluate the corrosion of metallic implants that can result in the release of corrosion products into bodily fluids causing possible adverse biological reactions. The determination of the chemical elements in the composition of the ISO 5832-1 stainless steel was performed by neutron activation analysis (NAA). The samples for electrochemical tests were grinded with silicon carbide paper up to #4000 finishing, followed by mechanical polishing with diamond paste. The open circuit potential measurements and anodic polarization curves were obtained in solution of 0.90 wt. % of NaCl and of simulated body fluid (SBF). The results indicated that the ISO 5832-1 stainless steel presented a high resistance to crevice corrosion in simulated body fluid solution but high susceptibility to this form of corrosion in the chloride solution.Artigo IPEN-doc 28360 Study of ph effect on AZ31 magnesium alloy corrosion for using in temporary implants2020 - SILVA, CAIO A.J. da; BRAGUIN, LILIAN N.M.; BERBEL, LARISSA O.; VIVEIROS, BARBARA V.G.; ROSSI, J.L.; SAIKI, M.; COSTA, I.Currently, magnesium alloys are gaining great interest for medical applications due to their degrading properties in the human body ensuring a great biocompatibility. These alloys also provide profitable mechanical properties due similarities with human bone. However, a difficulty in applying these materials in the biomaterials industries is the corrosion prior to cell healing. The effect of the chemical composition of Mg alloys on their corrosion behavior is well known. In this study, samples of AZ31 magnesium alloy were cut into chips for elemental chemical analysis by neutron activation analysis (NAA). Concentrations of the elements As, La, Mg, Mn, Na, Sb and Zn were determined in the AZ31 alloy. Visualization tests of agar corrosion development in various media, of 0.90% sodium chloride solution (mass), phosphate buffer saline (PBS) and simulated body fluid (SBF) were performed. Visualizations of the effect of agar gel corrosion revealed pH variation during the corrosion process due to the released into the cathode. The highest released of hydroxyl ions occurred in NaCl solution compared to PBS and SBF solutions indicating that NaCl solution was much more aggressive to the alloy compared to the others.Resumo IPEN-doc 27324 Estudo do comportamento frente à corrosão da liga de magnésio AZ31 de uso em implantes temporários utilizando soluções simuladoras de fluidos corpóreos2019 - SILVA, C.A.J.; BRAGUIN, L.N.M.; VIVEIROS, B.G.; BERBEL, L.O.; ROSSI, J.L.; COSTA, I.; SAIKI, M.Atualmente, ligas de magnésio estão ganhando grande interesse para aplicações médicas devido a sua propriedade de degradação no corpo humano, principalmente para aplicações de interesse como stents cardiovasculares e próteses ortopédicas. Estes implantes temporários fornecem uma estabilidade mecânica necessária para o reparo e corroem completamente após o tempo de vida útil e fim do tratamento. Contudo, uma dificuldade na aplicação destes materiais na indústria de biomateriais é a corrosão antecipada e precoce à cura celular. Amostras da liga de magnésio AZ31 foram cortadas em lascas e a técnica escolhida para análise química elementar foi a Análise por Ativação com Nêutrons (NAA). Irradiações de curta e longa duração foram realizadas nas amostras juntamente com padrões sintéticos no reator IEA-R1 em um fluxo de nêutrons térmicos abaixo de 4,0x1012 n cm-2s-1. Concentrações dos elementos As, La, Mg, Mn, Na, Sb e Zn foram determinadas na liga AZ31, calculadas pelo método comparativo. Para os ensaios de corrosão, as amostras foram limpas com álcool etílico, acetona e água purificada MilliQ por agitação ultrassônica, e, em seguida foram lixadas com lixas de SiC com granulometria de #500, #800, #1200, #2000 e #4000. Testes de visualização em ágar-ágar e imersão foram realizados em solução de cloreto de sódio 0,90 % (massa), solução tampão de fosfato (PBS) e solução simuladora de fluidos corpóreos (SBF) utilizando fenolftaleína como indicador ácido-base. A observação das superfícies das amostras, antes e após exposição às soluções, foi realizada por microscopia óptica (MO) e microscopia eletrônica de varredura (MEV). A superfície também foi observada após remoção dos produtos de corrosão por desmutting e irradiação para análise quantitativa pela técnica NAA. Visualizações em gel ágarágar revelaram aumento do pH local proveniente da liberação de íons hidroxila da reação catódica e menor liberação de íons ocorreu em SBF em comparação às soluções de NaCl e PBS. As micrografias da superfície evidenciaram a formação instantânea de uma camada de produtos de corrosão após uma hora de ensaio e o desmutting revelou microcavidades caracterizadas por pites.