REJANE MARIA PEREIRA DA SILVA
3 resultados
Resultados de Busca
Agora exibindo 1 - 3 de 3
Artigo IPEN-doc 28933 Corrosion behaviour of the 2098-T351 Al–Cu–Li alloy after different surface treatments2022 - BARBOZA, WANESSA das G.; MILAGRE, MARIANA X.; DONATUS, UYIME; MACHADO, CARULINE de S.C.; RAMIREZ, OSCAR M.P.; ARAUJO, JOAO V. de S.; SILVA, REJANE M.P. da; COSTA, ISOLDAThe effect of different surface treatments on the corrosion resistance of the AA2098 Al–Cu–Li alloy has been investigated. Surface characterization was performed using 3D optical profilometry, energy dispersive X-ray spectroscopy and scanning electron microscopy. The corrosion resistance of the 2098 alloy after the surface treatments was investigated in 0.1 mol L−1 NaCl solution by electrochemical techniques and microscopy. Corrosion results showed that the untreated and the chemically etched surfaces were more active than the mechanically abraded and mechanically polished surfaces owing to differences in the nature of the native oxides formed after the surface treatments. Corrosion rate and mode were also affected by how close the exposed surface was to the mid-thickness region of the AA2098-T351 plate relative to the actual top surface (before polishing). This is associated with the variation in the volume fraction and distribution of the T1 phase as the mid-thickness region of the AA2098-T351 plate is approached.Artigo IPEN-doc 28531 Influence of chloride ions concentration on the development of severe localised corrosion and its effects on the electrochemical response of the 2198-T8 alloy2021 - MACHADO, CARULINE de S.C.; SILVA, REJANE M.P. da; ARAUJO, JOAO V. de S.; MILAGRE, MARIANA X.; DONATUS, UYIME; VIVEIROS, BARBARA V.G. de; KLUMPP, RAFAEL E.; COSTA, ISOLDAThe development of severe localised corrosion (SLC) on the 2198-T8 alloy was investigated in solutions of various NaCl concentrations (0.001, 0.005 and 0.01 mol L−1). Immersion tests, optical profilometry, conventional and local electrochemical analyses were performed to evaluate the corrosion behaviour of the alloy. Immersion tests showed that the alloy is susceptible to SLC in all conditions, although the pits sizes were dependent on the solution concentration. The largest anodic areas, corresponding to SLC sites, were observed for the sample immersed in 0.001 mol L−1 NaCl, whereas pits with similar sizes were observed for the samples immersed in solutions with 0.005 and 0.01 mol L−1 of NaCl. Moreover, the maximum depth of attack was observed for the sample immersed in 0.001 mol L−1 NaCl. These results were in agreement with the scanning ionselective electrode technique (SIET) maps which showed stronger acidification on the sample exposed to 0.001 mol L−1 NaCl solution.Artigo IPEN-doc 25749 Comparison of the corrosion resistance of an Al–Cu alloy and an Al–Cu–Li alloy2019 - MILAGRE, MARIANA X.; DONATUS, UYIME; MACHADO, CARULINE S.C.; ARAUJO, JOAO V.S.; SILVA, REJANE M.P. da; VIVEIROS, BARBARA V.G. de; ASTARITA, ANTONELLO; COSTA, ISOLDAIn this study, the corrosion mechanisms of the AA2024-T3 and the AA2098-T351 were investigated and compared using various electrochemical techniques in 0.005 mol L−1 NaCl solution. The severe type of corrosion in the AA2098-T351 was intragranular attack (IGA) although trenching and pitting related to the constituent particles were seen. On the other hand, the AA2024-T3 exhibited severe localised corrosion associated with micrometric constituent particles, and its propagation was via grain boundaries leading to intergranular corrosion (IGC). Electrochemical techniques showed that the corrosion reaction in both alloys was controlled by diffusion. The non-uniform current distribution in both alloys showed that EIS was not a proper technique for comparing the corrosion resistance of the alloys. However, local electrochemical techniques were useful for the evaluation of the corrosion resistance of the alloys.