EIS study of the microstructure influence on the corrosion behaviour of AA 2198-T3 compared to AA 2198-T851 alloy
Carregando...
Data
Data de publicação:
2016
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
É parte de
INTERNATIONAL CONFERENCE ON SURFACE MODIFICATION TECHNOLOGIES, 30th
Exportar
Resumo
This paper deals with the study of the influence of the temper state on the electrochemical behavior of an high strength aluminum-lithium alloy. In particular the corrosion resistance of the AA2198 alloy in both T3 and T851 temper condition, has been evaluated by immersion tests as a function of immersion time in NaCl 0.01 mol.L-1. The evolution of the electrochemical behavior was monitored by electrochemical impedance spectroscopy (EIS) and surface observation by optical microscopy and Field Emission Gun- Scanning Electron Microscopy. The results indicated a higher electrochemical activity associated to the T851 treatment comparatively to the T3 one and this was ascribed to the more heterogeneous microstructure related to the first treatment. Severe localized corrosion was seen on the AA2198-T851 alloy after only few hours of exposure to the test medium. This type of corrosion was of the crystallographic type and was related to T1 (Al2LiCu) which is more electrochemically active than the matrix leading to localized attack. Pitting attack was seen on the AA2198-T3 alloy along the surface and it was located at the matrix-precipitates interface. The EIS results supported a faster kinetics and lower impedances associated to the AA2198-T851 comparatively to the AA2198-T3 alloy according to the surface observation along the test period.
Como referenciar
ARAUJO, J.V. de S.; QUEIROZ, F.M.; TERADA, M.; ASTARITA, A.; COSTA, I. EIS study of the microstructure influence on the corrosion behaviour of AA 2198-T3 compared to AA 2198-T851 alloy. In: INTERNATIONAL CONFERENCE ON SURFACE MODIFICATION TECHNOLOGIES, 30th, June 29 - July 1, 2016, Milan, Italy. Abstract... Disponível em: http://repositorio.ipen.br/handle/123456789/27324. Acesso em: 11 May 2024.