Characterization of Al-Si coating on press hardening steel (PHS) submitted to a natural weathering test
Carregando...
Data
Data de publicação:
2018
Orientador
TĂtulo da Revista
ISSN da Revista
TĂtulo do Volume
Ă parte de
Ă parte de
Ă parte de
Ă parte de
CONGRESSO BRASILEIRO DE ENGENHARIA E CIĂNCIA DOS MATERIAIS, 23.
Resumo
Targeting the reduction of stamped sheet metal thicknesses, higher mechanical
properties and better crash performance arise the hot stamping process as viable
alternative. This is achieved by heating up a steel blank to approximately 900 ÂșC for
the austenitization, soon after it is transferred to the hot stamping press, to be
conformed and cooled, aiming a martensitic microstructure, After that, the finished part
presents a tension strength about 1500 MPa. At the blank moving between furnace
and press, oxidation occurs on the sheet metal surface, and Al-Si coating has been
used as a good surface protection, which works against the oxidation process through
a protection barrier. For corrosion analysis and a behavior evaluation of the coating
subjected to climatic agents, the most trustful way is by means of the utilization of the
natural weathering test, in the present case in an urban environment. It was used
samples of 22MnB5 steel plates after different heat treatment conditions, achieving, in
this way, weathering results based in technical standards obtained by means of light
microscopy techniques.
Como referenciar
OLIVEIRA, B.G.; CUNHA, L.F.; ABBADE, L.; COLOSIO, M.A.; ROSSI, J.L.; COUTO, C.P.; LARA, J.C.; LIMA, V.F. Characterization of Al-Si coating on press hardening steel (PHS) submitted to a natural weathering test. In: CONGRESSO BRASILEIRO DE ENGENHARIA E CIĂNCIA DOS MATERIAIS, 23., 04-08 de novembro, 2018, Foz do Iguaçu, PR. Resumo... p. 4947-4947. DisponĂvel em: http://repositorio.ipen.br/handle/123456789/29561. Acesso em: 14 May 2024.