Influence of air quenching on apparent hardness of valve seat inserts obtained with AISI M2 high-speed steel powder
Carregando...
Data
Data de publicação:
2017
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
É parte de
ENCONTRO CIENTÍFICO DE FÍSICA APLICADA, 8.
Exportar
Resumo
The aim of this work consisted of evaluate the influence of heat treatment on sintered valve seat inserts
(VSI) obtained with the AISI M2 high-speed steel powder. The AISI M2 high-speed steel powder was
mixed with iron powder and additives such as manganese sulphide, zinc stearate, graphite and carbides.
The heat treatment of the VSI consisted of air quenching followed by double tempering it in seven different
equidistant temperatures, from 100 °C until 700 °C. The mechanical property was measured regarding the
VSI apparent hardness. The results indicated that the VSI obtained with the AISI M2 high-speed steel
powders mixtures showed the best results regarding its apparent hardness after air quenching and double
tempering it at 600 °C.
Como referenciar
GOMES, M.P.; SANTOS, I.P.; REIS, L.A.M.; CIONE, F.C.; COLOSIO, M.A.; ROSSI, J.L. Influence of air quenching on apparent hardness of valve seat inserts obtained with AISI M2 high-speed steel powder. In: ENCONTRO CIENTÍFICO DE FÍSICA APLICADA, 8., 4-7 de setembro, 2017, Vitória, ES. Anais... São Paulo, SP: Blucher Proceedings, 2017. p. 39-41. DOI: 10.5151/phypro-viii-efa-10. Disponível em: http://repositorio.ipen.br/handle/123456789/31222. Acesso em: 26 Apr 2024.