MARINA MARTINS MENNUCCI
6 resultados
Resultados de Busca
Agora exibindo 1 - 6 de 6
Artigo IPEN-doc 23955 Investigation of corrosion inhibitors for carbon steel used as reinforcement of concrete in artificial pore solution2005 - MENNUCCI, MARINA M.; COSTA, ISOLDAThe aim of this study was to evaluate the potential application of some chemical compounds as corrosion inhibitors for a carbon steel (CA-50) used as reinforcement of concrete in artificial pore solution. The tested compounds were sodium nitrite (1.5% in mass), hexamethylenetetramine (1.5% in mass) and benzotriazole (10-2 M). The techniques used in this investigation were electrochemical impedance spectroscopy (EIS), potentiodynamic polarization tests and open circuit potential measurements as a function of time. Each compound tested was added to a solution whose composition simulates that of the liquid inside the pores of concretes. To this solution was also added sodium chloride (3.5% in mass) to simulate the corrosive effects of marine atmospheres. The corrosion resistance of the carbon steel (CA-50) was evaluated in the solutions with and without the additives. A beneficial effect (corrosion resistance increase) was found for all types of inhibitors tested, but sodium nitrite and benzotriazole showed a significant inhibiting effect.Artigo IPEN-doc 23006 Investigação do potencial de aplicação do benzotriazol como inibidor de corrosão do aço carbono CA-50 em meio alcalino2006 - MENNUCCI, MARINA M.; COSTA, ISOLDAO objetivo deste trabalho foi avaliar a proteção frente à corrosão do aço carbono CA-50, devido ao ataque por íons cloreto em meio alcalino, por inibidores de corrosão, especificamente o nitrito de sódio e o benzotriazol. O aço CA-50 é um dos mais utilizados para armaduras em estruturas de concreto armado. A concentração utilizada, de ambos os aditivos, foi 0,5 % em massa. A eficiência dos compostos foi avaliada em meio que simula a composição química da água de poro com adição de cloreto, por métodos eletroquímicos, especificamente curvas de polarização potenciodinâmica e espectroscopia de impedância eletroquímica. Observou-se efeito benéfico nos dois tipos de inibidores testados, sendo que o benzotriazol obteve uma melhor eficiência na concentração adotada. Os resultados indicaram que o benzotriazol pode ser uma alternativa viável à substituição do nitrito em aplicações de construção civil, isto é, em meios alcalinos, principalmente devido às vantagens de menor toxicidade.Resumo IPEN-doc 22639 Evaluation of benzotriazole as corrosion inhibitor for carbon steel as reinforcement of concrete2006 - MENNUCCI, MARINA M.; COSTA, ISOLDAChlorides are very often the cause of localised corrosion in concretes due to their penetration from environment, mainly in marine atmospheres. Corrosion inhibitors is usually used as a corrosion prevention method against this form of corrosion in reinforced concretes. Nitrite is the main inhibitor for this purpose and it has been widely used for many years. However there are some limitations to its use such as environmental constraints due to the its toxic effect, mechanism of inhibition (anodic type), and also the relatively high costs of this type of additive. Research has been carried out in order to find other non toxic inhibiting additives for this application. In this investigation, benzotrizole (BTA), that is a well known corrosion inhibitor for stainless steel and carbon steels in acid media, has been evaluated as a possible corrosion inhibitor in the chloride containing alkaline environment typical of concretes in marine atmospheres. The corrosion inhibiting efficiency of BTA in the concentrations corresponding to 0.5%, 1% and 1.5% im massa, was investigated. These concentrations were added to a reference solution composed of 0.01N NaOH plus 0.05N KOH with 3.5% NaCl and the efficiency was estimated based on the corrosion rates obtained in this last solution. The effect of BTA was compared to the nitrite using solutions with similar concentration of the inhibiting additive. All reagents used for solutions preparation were of analytical grade. The test solutions were maintained at 20 o C under naturally aerated conditions. The surface of the carbon steel samples were prepared by ground with silicon carbide paper up to #600. After surface preparation the electrodes were immersed in the various test solutions used and the open circuit potential was measured as a function of time. The evolution of the corrosion resistance was evaluated by electrochemical impedance spectroscopy (EIS) from 1 until 6 days of immersion in the various test solutions. After this period, potentiodynamic polarization tests were carried out. A three-electrode cell arrangement was used for the electrochemical measurements, with Ag/AgCl and a platinum wire as reference and auxiliary electrodes, respectively. All potentials referred to in this work are with respect to Ag/AgCl. Polarization measurements were carried out using a Solartron SI 1287 potentiostat in the potential range from –0.25 V to 0.25 V versus the open circuit potential (Eocp) at a scan rate of 0.5 mV/s. The EIS tests were accomplished by means of a Solartron Model SI 1255 Frequency Response Analyzer coupled to a Princeton Applied Research (PAR) Model 273A Potentiostat/Galvanostat. The diagrams were obtained in potentiostatic mode at the corrosion potential, Ecorr, with an ac perturbation amplitude of 10 mV in the frequency range from 100 kHz to 10 mHz, with 8 points per decade. The EIS results for the solutions with various BTA contents after 6 days of immersion are shown in Figure 1 as Nyquist and Bode diagrams.Artigo IPEN-doc 10521 Avaliacao do efeito de inibidores na resistencia a corrosao de aco de contrucao civil2004 - MENNUCCI, M.M.; REIS, F.M.; HIGA, L.H.; COSTA, I.Dissertação IPEN-doc 11511 Avaliação da potencialidade de aditivos como inibidores de corrosão do aço carbono CA-50 usado como armadura de estuturas de concreto2006 - MENNUCCI, MARINA M.Neste trabalho, vários tipos de compostos foram testados com o objetivo de avaliar sua potencialidade para uso como inibidores de corrosão de armadura de aço carbono em concreto armado. Os aditivos testados foram benzoato de sódio, benzotriazol, carbonato de ítrio, polietilenoglicol, e hexametilenotetramina. Inicialmente foram realizados ensaios exploratórios para seleção dos candidatos potenciais entre os compostos testados com base na eficiência de inibição determinada por ensaios eletroquímicos, especificamente ensaios de polarização e espectroscopia de impedância eletroquímica. Os ensaios eletroquímicos foram realizados em uma solução sintética composta por 0,01N de hidróxido de sódio (NaOH) mais 0,05N de hidróxido de potássio (KOH), para simular a composição da solução dentro dos poros no concreto. O aditivo que apresentou melhor potencialidade para uso como inibidor de corrosão foi o benzotriazol (BTA). Após eliminação dos compostos que apresentaram potencial de plicação, e seleção do candidato com maior eficiência de inibição no meio de estudo, o efeito da sua concentração na resistência à corrosão foi avaliado. Soluções de nitrito de sódio foram também usadas nas mesmas oncentrações que as adotadas para as de BTA para efeito de comparação. O nitrito de sódio é um inibidor de corrosão já estabelecido para reforços de aço carbono em concreto, mas este tem sido associado com efeitos tóxicos. O benzotriazol (BTA) foi associado com eficiências de inibição sempre superiores às do nitrito de sódio nas mesmas concentrações. Um filme escuro e aderente foi formado na superfície do aço durante períodos longos de imersão no meio alcalino contendo BTA. Os resultados apontaram para o alto potencial de aplicação do BTA como aditivo inibidor da corrosão do aço em estruturas de concreto armado, podendo vir a substituir o nitrito nestas aplicações.Artigo IPEN-doc 14477 Evaluation of benzotriazole as corrosion inhibitor for carbon steel in simulated pore solution2009 - MENNUCCI, M.M.; BANCZEK, E.P.; RODRIGUES, P.R.P.; COSTA, I.