SYLVIO DIONYSIO DE SOUZA
23 resultados
Resultados de Busca
Agora exibindo 1 - 10 de 23
Artigo IPEN-doc 22538 Influences of plasma nitriding edge effect on properties of 316 L stainless steel2010 - OLZON DIONYSIO, M.; CAMPOS, M.; KAPP, M.; SOUZA, S. de; SOUZA, S.D. deSome rings of different colors are formed when cylindrical stainless steel samples are plasma nitrided. They appear because of a phenomenon known as the edge effect associated with this technique. In this paper, we discuss some of the characteristics of these rings formed in nitrided AISI 316 L austenitic stainless steel: dimension, microhardness, composition, and corrosion resistance. Two cylindrical samples with different diameters were plasma nitrided in a 80% H(2)-N(2) gas mixture, at a pressure of about 4 torr, for 4 h, at T(N) = 400 degrees C. One of the samples was surrounded by another ring-shaped sample, whose dimensions were chosen to contain the rings formed during the nitriding process. Consequently, rings of different dimensions were produced. The composition of samples was identified by conversion electron Mossbauer spectroscopy (CEMS) and Glancing angle X-ray diffraction (GAXRD). Regarding their relative dimensions, the rings showed similar characteristics, in spite of their different diameters. The samples displayed higher values of hardness in their rings than in their central regions. GAXRD detected peaks of Cr(2)N on the rings and of the expanded austenitic gamma(N) phase in the central region. CEMS results demonstrated the presence of the paramagnetic gamma(N) and epsilon phases. The proportion of these phases was consistent among the samples, regardless of their diameters. Concerning corrosion, the samples with a ring showed a poorer corrosion resistance than those without a ring. All results are in agreement with the presence of chromium nitride Cr(2)N on the ring of each sample. Published by Elsevier B.V.Artigo IPEN-doc 22540 Mossbauer spectroscopy study on the corrosion resistance of plasma nitrided ASTM F138 stainless steel in chloride solution2010 - SOUZA, S.D. de; OLZON DIONYSIO, M.; BASSO, R.L.O.; SOUZA, S. deArtigo IPEN-doc 20447 Study of expanded austenite formed in plama nitrided AISI 316L samples, using syncchrotron radiation diffraction2014 - CAMPOS, MARCELO; SOUZA, SYLVIO D. de; MARTINEZ, LUIS G.; OLZON-DIONYSIO, MARISTELAResumo IPEN-doc 04721 Caracterizacao de ceramicas ferroeletricas pela tecnica TDPAC1996 - MOTTA, E.F.; SOUZA, S.D.; OLZON DIONYSIO, M.; CARBONARI, A.W.Resumo IPEN-doc 02882 Caracterizacao de ceramicas tipo PZT pela tecnica de correlacao angular perturbada1996 - MOTTA, E.F.; SOUZA, S.D.; OLZON DIONYSIO, M.; CARBONARI, A.W.Resumo IPEN-doc 02880 Estudo do campo hiperfino magnetico nas ligas de Heusler do tipo Cosub(2)ScZ(Z=Ge,Sb)1995 - MIOLA, E.J.; OLZON DIONYSIO, M.; SOUZA, S.D.; SAXENA, R.N.; CARBONARI, A.W.; PENDL JUNIOR, W.Resumo IPEN-doc 15860 Influencia da pressao no processo de nitretacao a plasma de aco inoxidavel austenitico AISI 316L2010 - SOUZA, S. de; CAMPOS, M.; SOUZA, S.D. de; DIONYSIO, M.O.Resumo IPEN-doc 15868 Estudo da estrutura da fase '&#'933;N formada na nitretacao a plasma do aco inovidavel AISI 316L2010 - CAMPOS, M.; SOUZA, S.D. de; MARTINEZ, L.G.; DIONYSIO, M.O.Resumo IPEN-doc 15883 Influencia da temperatura e tempo na nitretacao a plasma do aco inoxidavel AISI 316L2010 - CAMPOS, M.; SOUZA, S.D. de; MARTINEZ, L.G.; DIONYSIO, M.O.Resumo IPEN-doc 04795 Campo hiperfino magnetico nas ligas de Heusler Cosub(2)YZ (Y=V, Nb, Ta, Cr, Z=Al, Ga)1993 - PENDL JUNIOR, W.; CARBONARI, A.W.; ATTILI, R.N.; SAXENA, R.N.; SOUZA, M.O.D.; SOUZA, S.D.
- «
- 1 (current)
- 2
- 3
- »