ELINER AFFONSO FERREIRA
23 resultados
Resultados de Busca
Agora exibindo 1 - 10 de 23
Artigo IPEN-doc 23028 Heat treatment and microstructural studies of LaNi-Type battery electrode alloys2017 - FERREIRA, E.A.; BARBOSA, L.P.; FARIA, R.N.The effects of annealing on the microstructures and electrochemical characteristics of a La0.7Mg0.3Al0.3Mn0.4Co0.5Ni3.8 hydrogen storage alloy have been studied. The heat treatment by vacuum annealing was carried out at 700 oC, 800 oC, 900 oC and 1000 oC. The microstructure and phase composition of the alloy have been investigated using inductively coupled plasma - atomic emission spectrometry (ICP-AES), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and X-ray diffraction analysis (XRD). The battery anode was prepared using a mixture of the pulverized alloy with carbon black and polytetrafluoroethylene as a binder.Tese IPEN-doc 21817 Estudo da hidrogenação para pulverização de ligas à base de terras raras com Nb para eletrodos de hidreto metálico2013 - FERREIRA, ELINER A.Neste trabalho foram estudadas as series de ligas La0,7Mg0,3Al0,3Mn0,4Co(0,5-x)NbxNi3,8 (x =0 a 0,5) e La0,7Mg0,3Al0,3Mn0,4Nb(0,5-x)Ni(3,8-x) (x =0,3; 0,5 e 1,3), como eletrodo negativo de baterias de Níquel Hidreto Metálico. A pulverização das ligas foi realizada com duas pressões de H2 (2 bar e 9 bar). A capacidade de descarga das baterias de níquel hidreto metálico foi analisada pelo equipamento de testes elétricos Arbin BT-4. As ligas, no estado bruto de fusão, foram analisadas por microscopia eletrônica de varredura (MEV), espectroscopia de energia dispersiva (EDS) e difração de raios-X. Com o aumento da concentração de nióbio nas ligas nota-se a diminuição da estabilidade cíclica das baterias e da capacidade máxima de descarga. A capacidade de descarga máxima obtida foi para a liga La0,7Mg0,3Al0,3Mn0,4Co0,5Ni3,8 (45,36 mAh) e a bateria que apresentou a melhor performance foi a liga La0,7Mg0,3Al0,3Mn0,4Co0,4Nb0,1Ni3,8 (44,94 mAh).Artigo IPEN-doc 20829 Effect of Sn substitution for Co on microstructure and electrochemical performance of ABsub(5) type Lasub(0.7)Mgsub(0.3)Mnsub(0.4)Cosub(0.5)-sub(x)Snsub(3.8)(x=0-0.5) alloys2015 - CASINI, JULIO C.S.; GUO, ZAIPING; LIU, HUA K.; FERREIRA, ELINER A.; FARIA, RUBENS N.; TAKIISHI, HIDETOSHIResumo IPEN-doc 18450 Microstructure and electrochemical properties of the La0.7Mg0.3Al0.3Mn0.4Co0.5NbxNi(3.8-x)(x=0.5-1.8) hybride alloys2012 - FERREIRA, E.A.; TAKIISHI, H.; FARIA R.N.Resumo IPEN-doc 18449 Effect of Nb content on the structural and electrochemical properties of the La0.7Mg0.3Al0.3Mn0.4Co(0.5-x)NbxNi3.8(x=0-0.5) hydrogen storage alloys2012 - FERREIRA, E.A.; TAKIISHI, H.; FARIA R.N.Resumo IPEN-doc 17966 Study on hydrogenation of the La0.7-xMgxPr0.3Al0.3Mn0.4Co0.5Ni3.8 (x=0.0, 0.1 and 0.3) alloys for nickel - metal hydride batteries2011 - CASINI, J.C.S.; GALDINO, G.S.; FERREIRA, E.A.; FARIA, R.N.; TAKIISHI, H.Artigo IPEN-doc 12584 The effect of milling time upon microstructures of Pr-Fe-B HD sintered magnets prepared by a low cost powder technique2006 - SOARES, E.P.; FERREIRA, E.A.; PERIGO, E.A.; TAKIISHI, H.; FARIA, R.N.Artigo IPEN-doc 12487 The effect of milling time upon microstructures of Pr-Fe-B HD sintered magnets prepared2007 - SOARES, E.P.; FERREIRA, E.A.; PERIGO, E.A.; TAKIISHI, H.; FARIA, R.N.Artigo IPEN-doc 12485 The effect of the processing temperature on the microstructures of Pr-Fe-Co-Nb HDDR magnets2007 - SILVA, S.C.; FERREIRA, E.A.; FARIA, R.N.; TAKIISHI, H.Artigo IPEN-doc 12483 Microstructure and magnetic properties of PrFeCoBNb sintered magnets produced from Hd and HDDR powder2007 - FERREIRA, E.A.; SILVA, S.C.; PERIGO, E.A.; FARIA, R.N.; TAKIISHI, H.
- «
- 1 (current)
- 2
- 3
- »