JOSE ANTONIO BATISTA DE SOUZA
2 resultados
Resultados de Busca
Agora exibindo 1 - 2 de 2
Artigo IPEN-doc 29863 Manufacturing high-uranium-loaded dispersion fuel plates in Brazil2024 - DURAZZO, MICHELANGELO; SOUZA, JOSE A.B.; CARVALHO, ELITA F.U. de; RESTIVO, THOMAZ A.G.; GENEZINI, FREDERICO A.; LEAL NETO, RICARDO M.The Nuclear and Energy Research Institute (IPEN-CNEN/SP) has developed and made available for routine production the technology for manufacturing dispersion-type fuel elements for research reactors. However, the fuel produced is limited to a uranium loading of 2.3 gU/cm3 (U3O8) or 3.0 gU/cm3 (U3Si2). To reduce Brazil’s dependence on foreign sources of Mo-99, the Brazilian government plans to construct a new research reactor, the 30 MW open pool Brazilian Multipurpose Reactor (RMB), which will mainly produce domestic Mo-99. Low-enriched uranium fuel will be used in the RMB, and increasing uranium loading will be important to increase the reactor core’s reactivity and fuel life. Uranium loadings of 3.2 gU/cm3 for the U3O8-Al and 4.8 gU/cm3 for the U3Si2-Al are considered the technological limit and have been well demonstrated worldwide. This work aimed to study the manufacturing process of these two highly uranium-loaded dispersion fuels and redefine current procedures. Additionally, UMo-Al dispersion fuel has been extensively studied globally and is likely to be the next commercially available technology. This new fuel utilizes a dispersion of UMo alloy with 7–10 wt% Mo, resulting in a uranium loading between 6 and 8 gU/cm3. We also studied this fuel type for potential use in the RMB research reactor. This work outlines the primary procedures for manufacturing these three types of fuels and the necessary adjustments to IPEN-CNEN/SP current technology. The manufacturing process proved to be well adapted to these new fuels, requiring only minor modifications. A comparison was made of the microstructures of fuel plate meat using three types of uranium compounds. The microstructures of U3Si2-Al and U10Mo-Al dispersions were found to be adequate, while that of U3O8-Al meat deviated significantly from the concept of an ideal dispersion.Artigo IPEN-doc 23162 Effect of porosity on the manufacturing of U3O8-Al dispersion fuel plates2017 - DURAZZO, M.; SOUZA, J.A.B.; CARVALHO, E.F.U. de; RIELLA, H.G.The pore volume present in the starting fuel meat of dispersion fuel plates influences the behavior of its deformation during the fuel plate fabrication by rolling to a great extent. This study was carried out to investigate the influence of pore content in the starting fuel meat on the manufacturing of aluminum-base dispersion fuel plates. Factors that affect the residual porosity present in the meat of the fuel plate were investigated. Results showed that the residual pore volume of aluminum-base dispersion-type U3O8-Al fuel plates depends on the characteristics of the starting fuel meat, which is fabricated by pressing. The residual pore volume depends on the U3O8 concentration. For a particular U3O8 concentration, the rolling process establishes a constant pore volume, which is called equilibrium porosity. The equilibrium porosity is insensitive to the initial pore volume present in the starting fuel meat. The research showed that fuel meat integrity was greatly influenced by the initial porosity of the fuel meat. U3O8-Al dispersion fuel plates were successfully fabricated with uranium loading above 3.0 gU/cm(3). This uranium loading is equivalent to the one used in the U3Si2-Al dispersion fuel, currently operating at the lEA-R1 research reactor of the Nuclear and Energy Research Institute - IPEN/CNEN-SP. The U3O8-Al dispersion fuel can substitute the silicide fuel with advantages such as lower price and simpler manufacturing process.