Elaboração mecânica do intermetálico TiFe para armazenagem de hidrogênio
Carregando...
Data
Data de publicação:
2016
Autores IPEN
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
É parte de
CONGRESSO BRASILEIRO DE ENGENHARIA E CIENCIA DOS MATERIAIS, 22.
Exportar
Resumo
Elementary powders of Ti and Fe in the stoichiometric ratio 50:50 were submitted to mechanical alloying for 2, 6, 10 and 20 h in a planetary ball mill. The synthesis of TiFe intermetallic with high yield was achieved for all milling times. The structural characterization of the samples revealed the trend of the particles to form agglomerates and the formation of cracks. H-absorption capacities of 0,74; 0,90; 0,97 and 0,95 wt. % (at room temperature and 20 bar of H2) were obtained for processing times of 2, 6, 10 and 20 h, respectively, without using a thermal activation process after milling.
Como referenciar
VEGA, L.E.R.; LEIVA, D.R.; SILVA, W.B.; LEAL NETO, R.M.; ISHIKAWA, T.T.; BOTTA, W.J. Elaboração mecânica do intermetálico TiFe para armazenagem de hidrogênio. In: CONGRESSO BRASILEIRO DE ENGENHARIA E CIENCIA DOS MATERIAIS, 22., 06-10 de novembro, 2016, Natal, RN. Anais... p. 5048-5058. Disponível em: http://repositorio.ipen.br/handle/123456789/27246. Acesso em: 19 Feb 2025.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.