Investigação da corrosão localizada das ligas dissimilares (2024-T3 e 7475-T651) soldadas por FSW
Carregando...
Data
Data de publicação:
2016
Autores IPEN
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
É parte de
CONGRESSO BRASILEIRO DE ENGENHARIA E CIENCIA DOS MATERIAIS, 22.
Exportar
Resumo
The aeronautic industry has shown great interest in joining aluminum dissimilar alloys used in different parts of the aircraft. The Friction Stir Welding (FSW) process was developed has been considered as an effective alternative to con-ventional techniques for welding of aluminum alloys. This technique results in different microstructural areas affecting the corrosion resistance of the material. In this work, the corrosion resistance of the different zones formed in the 2024-T3 and 7475-T761 alloys welded by FSW has been investigated by electro-chemical techniques. An electrochemical cell with a small area exposed to the electrolyte (o-ring with 1.0 mm diameter) was used to allow testing the different zones generated, separately. Test solution consisted of 0.1M Na2SO4 + 1mM NaCl. The electrochemical results showed lower corrosion resistance associat-ed to the nugget zones. Besides, the TMAZ of the two alloys, mainly of the 7475-T651 presented corrosion resistance inferior to the BM and HAZ zones.
Como referenciar
ABREU, C.P.; MELO, H.G. de; PEBERE, N.; VIVIER, V.; COSTA, I. Investigação da corrosão localizada das ligas dissimilares (2024-T3 e 7475-T651) soldadas por FSW. In: CONGRESSO BRASILEIRO DE ENGENHARIA E CIENCIA DOS MATERIAIS, 22., 06-10 de novembro, 2016, Natal, RN. Anais... p. 6653-6663. Disponível em: http://repositorio.ipen.br/handle/123456789/27295. Acesso em: 26 Apr 2024.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.