Study of the weathering of high melt strength polypropylene (HMS-PP)

Abstract

One of the reasons for the good acceptance of the commercial PP is the fact that market requires products with features of “engineering plastics” with prices in the range of commodities. High melt strength polypropylene (HMSPP) grades are produced by radiation process and have improved rheology for melt blow processes. The melt strength (MS) properties of a polymer increase with molecular weight and with long chain branching due to the increase in the entanglement level. The main scope of this study was to evaluate the stability of HMS-PP prepared by gamma radiation with doses of 12.5, 20 kGy in comparison with virgin PP. Many variables influence the rate of degradation of polymers by photo-oxidation. The irradiance and permeability to oxygen are the most important factors but other factors such as temperature and moisture have also influenced the degradation rates. Polypropylenes are sensitive to oxidation due to the presence of the tertiary carbon atom. Therefore, effective stabilization against oxidation (thermo and photo oxidation) is required. The samples submitted to the natural aging for a period of six months were characterized by: tensile test, thermogravimetry analysis (TGA), optical microscopy, scanning electronic microscopy (SEM) and infrared spectroscopy (FTIR). SEM analysis showed particular aspects of cracks on the surface. The loss of tensile strength is associated to the presence of fractures. The results showed that pronounced oxidation followed by chain scission occur at the initial periods of weathering exposition of the HMS-PP.