Evaluation of environmental aging of polypropylene irradiated versus pristine

Abstract

Polypropylene (PP) is the most common thermoplastic resin of the plastic market due to its very interesting physical, chemical and processing properties at very low market price, however after its use the resin does not degrade in the environment or it degrades at very low rate. This study has the objective of comparing the environmental exposure of PP irradiated with 20 kGy and pristine PP. Dumbbell samples were manufactured by injection molding and exposed to the environment during 90 days; another one set was subjected to gamma irradiation at 20 kGy total dose and exposed at the same conditions too. The samples were characterized by mechanical testing, visual inspection, infrared spectroscopy (IR), scanning electron microscopy (SEM) and differential scanning calorimetry (DSC). The irradiated samples, after environmental aging, showed oxidation and presence of cracks in samples of the PP 20 kGy.