Resumo
Rare earths (RE) have been used to improve high temperature oxidation resistance of
chromium dioxide and alumina forming alloys. The RE can be added to the alloy as elements
or as oxide to form dispersions. It can also be applied as a RE oxide coating to the surface of
the alloy. In this investigation the sol-gel technique was used to prepare sols of the RE oxides
as it produces nanocrystalline oxide particles. In an effort to increase further the oxidation
resistance of high temperature alloys, optimization of RE oxide additions to the alloy surface
has been attempted. This paper presents the effect of nanocrystalline oxide gel coatings of
CeO2, Nd2O3, Pr2O3, CeO2 + Nd2O3, CeO2 + Pr2O3 and Pr2O3 + Nd2O3 on the oxidation
behavior of Fe20Cr5Al alloys at 1100 °C. The individual oxides decreased oxidation rate.
However, the CeO2 + Nd2O3 mixture did not increase oxidation resistance of the alloy further,
compared to those with either one of these two rare earth oxides. The Pr2O3 + CeO2 mixture
increased oxidation resistance of the alloy markedly where as the mixture Nd2O3 to Pr2O3 had
no significant effect. The differences in the influence of a specific rare earth oxide or a
mixture are attributable to differences in the ionic radii of the RE and the morphology as well
as the crystallite sizes of the RE oxides.
Como referenciar
FERNANDES, STELA M.C.; CORREA, OLANDIR V.; RAMANATHAN, LALGUDI V. Effect of nanocrystalline mixed rare earth oxide coatings on the high temperature oxidation behavior of Fe20Cr5Al alloy. In: CONGRESSO BRASILEIRO DE CORROSÃO, 34.; INTERNATIONAL CORROSION MEETING, 5th.; CONGRESO IBEROAMERICANO DE CORROSIÓN Y PROTECCIÓN, 10th.; CONCURSO DE FOTOGRAFIA DE CORROSÃO E DEGRADAÇÃO DE MATERIAIS, 19.; EXPOSIÇÃO DE TECNOLOGIAS PARA PREVENÇÃO E CONTROLE DA CORROSÃO, 34, 19-23 de maio, 2014, Fortaleza, CE. Anais... Rio de Janeiro, RJ: Associação Brasileira de Corrosão – ABRACO, 2014. Disponível em: http://repositorio.ipen.br/handle/123456789/26437. Acesso em: 13 Mar 2025.