Effect of electron-beam irradiation on Nylon-6/diamond coated CNTS composite fiber
Carregando...
Data
Data de publicação:
2013
Autores IPEN
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
É parte de
SAMPE Tech
Exportar
Resumo
Polyamides (Nylon-6) are engineering plastic with excellent properties which are useful in several industrial applications and are valued for their high strength and processability. The addition of filler such as diamond coated Carbon Nano Tubes (CNTs) to form molded composites has increased the range of polyamide applications due to the resulting increase in strength. The effects of electron-beam irradiation on these thermoplastic nanocomposites are either increases the cross-linking or causes chain scission. In this study, DN-coated CNTs were synthesized using sonochemical technique in the presence of cationic surfactant CTAB. These hybrid nanoparticles were characterized using TEM analysis. The nanoparticles were then introduced into Nylon-6 polymer through a melt extrusion process to form nanocomposite fibers that were tested for their mechanical & thermal properties (e.g. tensile and Differential Scanning Calorimetry). These composites were further exposed to the electron-beam (160 KGy, 132 KGy and 99 KGy) using a 1.5 MeV electron beam accelerator, at room temperature, in presence of air and tested for their thermal and mechanical properties. The ultimate tensile strength were found to be 521 MPa, 690 MPa and 425 MPa for radiated (99 KGy,132 KGy and 160 KGy) DN/CNTs/Nylon-6 single fibers as compared to 346 MPa for DN/CNTs/Nylon-6 single fibers without irradiation and 240 MPa for neat Nylon-6 single fibers respectively. Differential Scanning Calorimetry (DSC) analysis results were showed that degree of cure was increased because of cross-linking which was expected at high electron-beam radiation dose.
Como referenciar
IMAM, MUHAMMAD A.; GOMES, M.G.; MOURA, ESPERIDIANA A.B.; JEELANI, SHAIK; RANGARI, VIJAY K. Effect of electron-beam irradiation on Nylon-6/diamond coated CNTS composite fiber. In: SAMPE Tech, October 21-24, 2013, Wichita, KS, USA. Proceedings... Disponível em: http://repositorio.ipen.br/handle/123456789/27646. Acesso em: 19 Mar 2025.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.