Influência da microestrutura na resistência ao choque térmico do SIC
Carregando...
Data
Data de publicação
2016
Autores IPEN
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
É parte de
CONGRESSO BRASILEIRO DE CERAMICA, 60.
Exportar
Resumo
The aim of this study is to analyze the influence of microstructure on thermal shock resistance of liquid phase sintered SiC, as this is a very required property in various technological applications. The microstructure can influence the thermal shock resistance because large grains tend to generate toughening mechanisms, reducing damage to the material. For this analysis, samples with 90 % SiC 10 % + (Y2O3:Al2O3) in the proportions 1: 3 and 1: 4 mole, were compacted and sintered at 1750 ° C , 1850 ° C and 1950 ° C. The thermal shock was performed by heating the sample in a tubular furnace and quenched in water. Damages caused by thermal shock were evaluated by monitoring the elastic modulus of samples. Micrographs were done by electron microscope and grain size distribution at Quantikov software. The samples sintered at 1950 °C have greater grain size and, consequently, greater thermal shock resistance.
Como referenciar
MELLO, R.M.; BRESSIANI, A.H.A. Influência da microestrutura na resistência ao choque térmico do SIC. In: CONGRESSO BRASILEIRO DE CERAMICA, 60., 15-18 de maio, 2016, Águas de Lindóia, SP. Anais... p. 1153-1164. Disponível em: http://repositorio.ipen.br/handle/123456789/27307. Acesso em: 30 Dec 2025.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.