The aim of this work was to evaluate the microstructure changes occurred in the alloys FeCr,
FeCrY, FeCrAl and FeCrAlY after exposition of 48h at 1000°C in a N2-4%H2 atmosphere,
often used in steel sintering furnaces in industries. The characterization was performed in a
scanning electron microscopy coupled with dispersive energy analysis, and X-ray diffraction.
It was observed the formation of chromium oxide and chromium nitride in the FeCr and
FeCrY alloys in the bulk of the sample as internal oxidation. FeCrAl alloy presented
chromium and aluminum oxide and nitride at the surface and in the bulk of the alloy.
FeCrAlY alloy formed a -alumina layer in the surface that maintained at the alloy protected
from further oxidation.
Como referenciar
PILLIS, MARINA F.; RAMANATHAN, LALGUDI V. Avaliacao microestrutural da liga FeCr apos exposicao a alta temperatura em atmosfera Nsub(2)-4%Hsub(2). In: CONGRESSO BRASILEIRO DE CORROSAO, 30.; INTERNATIONAL CORROSION MEETING, 2rd, 24-28 de maio, 2010, Fortaleza, CE. Proceedings... Disponível em: http://repositorio.ipen.br/handle/123456789/17989. Acesso em: 31 Dec 2025.