Substratos de compósitos cerâmicos no sistema Si-Al-O-N-C preparados com precursores poliméricos
Carregando...
Data
Data de publicação
2000
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
É parte de
CONGRESSO BRASILEIRO DE ENGENHARIA E CIENCIA DOS MATERIAIS, 14.
Exportar
Resumo
One of the advantages of the active filler controlled polymer pyrolysis process (AFCOP) is
the application of the various plastic shaping technologies. In the current work, doctor blade
technique was combined with polymer pyrolysis process to produce ceramic composite
substrates. Substrates with thickness of 600 µm were prepared spreading a slurry on acetate
film. The slurry composition comprises 60 vol% of polysiloxane and 40 vol% of active filler
divided in metallic Al and Si. Due to the polymer phase in the starting mixture a flexible and
thin substrate can be easily formed. The substrates were pyrolysed in nitrogen atmosphere up
to 1500 °C for 2 h resulting in a thin parallel substrate. SiAlON, AlN and β-SiC are among
the identified crystalline phases after pyrolysis. The substrates shown open porosity higher
than 25%, and thermal expansion coefficient lower than commercially available alumina
substrates.
Como referenciar
ROCHA, R.M.; SCHEFFLER, M.; GREIL, P.; BRESSIANI, J.C.; BRESSIANI, A.H.A. Substratos de compositos ceramicos no sistema Si-Al-O-N-C preparados com precursores polimericos. In: KIMINAMI, C.S. (ed.); EIRAS, J.A. (ed.); PESSAN, L.A. (ed.); TOMASI, R. (ed.). In: CONGRESSO BRASILEIRO DE ENGENHARIA E CIENCIA DOS MATERIAIS, 14., 3-6 dez, 2000, Sao Pedro, SP. Anais... p. 12101-12109. Disponível em: http://repositorio.ipen.br/handle/123456789/13392. Acesso em: 30 Dec 2025.