LUIZA MELLO DE PAIVA CAMPOS
4 resultados
Resultados de Busca
Agora exibindo 1 - 4 de 4
Resumo IPEN-doc 26936 Estudo da liberação de clorexidina incorporada em nanopartículas de montmorilonita em compósitos a base de BisGMA/TEGDMA2016 - CAMPOS, L.M.P.; BOARO, L.C.C.; SANTOS, T.M.R.; VARCA, G.H.C.; SANTOS, L.K.G.; LUGAO, A.B.; PARRA, D.F.O objetivo desse estudo foi desenvolver nanocompósitos experimentais adicionados com nanopartículas de Montmorilonita (MMT) incorporadas com diacetato de clorexidina (CHX) como carga, em uma matriz polimérica a base de BisGMA/TEGDMA (1:1). Foram confeccionados compósitos experimentais (n=5) adicionados com carga nas concentrações de 0.01, 0.5, 2 e 10% em massa (p/p). A liberação da CHX foi avaliada in vitro em uma solução neutra (pH 7, 50mm) a 37 oC, por 366 horas. A quantificação de CHX foi avaliada por espectrofotometria de UV (λ=255 nm). A formação de nanocompósitos foi avaliada por meio das metodologias Microscopia Eletrônica de Transmissão (MET) e Difração de Raio-X (DRX). Foi observada uma liberação de fármaco constante em todos os grupos analisados, de 0 a 366 horas. Ao atingir 366 horas, o grupo adicionado com 0,01% de carga apresentou 0.126 g.L-1 de liberação de CHX, o grupo com 0.5% apresentou 0.139 g.L-1, o grupo com 2% apresentou 0.150 g.L-1 e o grupo com 10% apresentou 0.151 g.L-1. Observou-se por meio do DRX e MET que houve intercalação entre a MMT (adicionada com CHX) e a matriz polimérica, em todos os grupos avaliados. Concluiu-se que houve a formação de nanocompósitos e que os mesmos promoveram constante liberação de CHX entre 0 a 366 horas. Esses resultados evidenciaram um forte potencial no desenvolvimento de nanocompósitos contendo fármaco antimicrobiano para aplicação odontológica.Artigo IPEN-doc 22803 Evaluation of flexural modulus, flexural strength and degree of conversion in BISGMA/TEGDMA resin filled with montmorillonite nanoparticles2016 - CAMPOS, LUIZA M.P.; BOARO, LETICIA C.; SANTOS, TAMIRIS M.R.; MARQUES, PAMELA A.; ALMEIDA, SONIA R.Y.; BRAGA, ROBERTO R.; PARRA, DUCLERC F.This study had as its main objective to evaluate the flexural properties (strength and modulus) and degree of conversion of a dimethacrylate resin containing different amounts of nanoparticulated clay Montomorillonite (MMT) as filler. A series of composites containing similar amounts (in volume) of barium glass particles was also tested as control data. Eight formulations with polymeric matrix-based BisGMA/TEGDMA (Bisphenol A Bis(2-hydroxy-3 methacryloxypropyl)Ether/ Triethyleneglycol Dimethacrylate), four added with MMTand four added with barium glass in the volume concentration of 20, 30, 40 and 50 vol% were studied. The degree of conversion was determined using near-IR spectroscopy. Elastic modulus and flexural strength were determined by the three-point bending test. The dispersion of MMT nanoparticles was determined by means of X-ray diffraction and transmission electron microscopy analysis. The fillers montomorillonite and barium glass interacted with polymer matrix-based BisGMA/TEGDMA in a distinct manner. Although the addition of montomorillonite nanoparticles resulted in similar degree of conversion and higher elastic modulus values at all concentrations tested, only at the 20 vol% the flexural strength was statistically higher, compared to the control groups filled with barium glass. This could be related to the need of concentration optimization of montomorillonite for each type of polymer matrix in order to adjust or improve mechanical properties. The addition of low concentrations (Artigo IPEN-doc 21255 Influence of ionizing radiation on the mechanical properties of BisGMA/TEGDMA based experimental resin2015 - CAMPOS, L.M.P.; BOARO, L.C.; SANTOS, L.K.G.; PARRA, D.F.; LUGAO, A.B.Artigo IPEN-doc 19819 DH and ESPI laser interferometry applied to the restoration2014 - CAMPOS, L.M.P.; PARRA, D.F.; VASCONCELOS, M.R.; VAZ, M.; MONTEIRO, J.