ALBERTO BLAY
10 resultados
Resultados de Busca
Agora exibindo 1 - 10 de 10
Artigo IPEN-doc 20860 Optical properties of human radicular dentin: ATR-FTIR characterization and dentine tubule direction influence on radicular post adhesion2015 - QUINTO JUNIOR, JOSE; ZAMATARO, CLAUDIA B.; BENETTI, CAROLINA; DIAS, DERLY A.; BLAY, ALBERTO; ZEZELL, DENISE M.Artigo IPEN-doc 20442 Attenuated total reflection fourier transform infrared (ATR-FTIR) spectroscopic analysis of regenerated bone2014 - BENETTI, CAROLINA; KAZARIAN, SERGEI G.; ALVES, MARCO A.V.; BLAY, ALBERTO; CORREA, LUCIANA; ZEZELL, DENISE M.Artigo IPEN-doc 20280 Surface alterations of zirconia and titanium substrates after Er, Cr:YSGG irradiation2015 - MIRANDA, PERSIO V.; RODRIGUES, JOSE A.; BLAY, ALBERTO; SHIBLI, JAMIL A.; CASSONI, ALESSANDRAThis study investigated changes in the roughness parameters (Sa in μm2 and Ra in μm) of yttrium-stabilized tetragonal zirconia polycrystal (Y-TZP) and large-grit sandblasted acid-etched (SLA) titanium (TI) materials after decontamination by erbium chromium-doped:yttrium, scandium, gallium, and garnet (Er,Cr:YSGG) laser irradiation. Twenty disks were analyzed in this study: 10 disks of Y-TZP (5 mm in diameter and 3 mm in height), standardized with CAD–CAM procedures, and 10 disks of SLA TI (5 mm in diameter and 4 mm in thickness). Disks were randomized into four groups (n=5), according to whether laser irradiation was performed: Y-TZP_G1 and TI_G1 were not treated by laser (control groups), whereas Y-TZP_G2 and TI_G2 were irradiated with Er,Cr:YSGG laser (1.5 W/20 Hz, air–water cooling proportion of 80 %/25 %). The surface topography of the disks was analyzed by confocal light microscopy. The mean Sa and Ra values were calculated from five profiles from each group. The results were statistically analyzed by t-test at the 95 % confidence level (α=0.05). For Y-TZP, the Sa results (in mean±SD) for Y-TZP_G1 and Y-TZP_G2 were 2.60±1.1 and 0.80±0.17 μm2 , respectively, and the Ra results were 2.01± 0.71 and 0.18±0.15 μm, respectively (both p<.05). For SLA TI, the Sa results for TI_G1 and TI_G2 were 1.99±0.5 and 3.37±0.75 μm2 , respectively, and the Ra results were 1.78± 0.53 and 3.84±0.63 μm, respectively (both p<.05). Er,Cr:YSGG laser irradiation alters the surface roughness of zirconia and SLA TI.Resumo IPEN-doc 09176 Effects of visible and NIR low intensity lasers on implant osseointegration in vivo2002 - BLAY, A.; BLAY, C.C.; GROTH, E.B.; ZEZELL, D.M.; SENDYK, W.R.; TUNCHEL, S.Resumo IPEN-doc 17461 An alternative approach for reopening implant surgery2011 - BLAY, ALBERTO; BLAY, CLAUDIA C.; TUNCHEL, SAMY; SHIBLI, JAMIL A.; ZEZELL, DENISE M.Resumo IPEN-doc 10369 Esmalte dental bovino irradiado com laser de Er, Cr:YSGG2004 - ANA, P.A.; MIYAKAWA, W.; BLAY, A.; ZEZELL, D.M.Resumo IPEN-doc 06496 Efeitos da radiacao laser em baixa intensidade no mecanismo de osseointegracao de implantes: estudo in vivo2002 - BLAY, A.; BLAY, C.C.; GROTH, E.B.; TUNCHEL, S.; SENDYK, W.R.; ZEZELL, D.M.Resumo IPEN-doc 19169 Association of fluoride and Er, Cr:YSGG laser irradiation provides enamel resistance to low pH environment2013 - ZAMATARO, CLAUDIA B.; BENETTI, CAROLINA; ANA, PATRICIA A.; BLAY, ALBERTO; PEREIRA, THIAGO M.; ZEZELL, DENISE M.Resumo IPEN-doc 15442 Quantitative microanalysis of enamel irradiated with Nd:YAG and Er, Cr:YSGG laser2006 - ZEZELL, D.M.; KAUFFMAN, C.M.F.; ANA, P.A.; BLAY, A.; SALVADOR, V.L.R.; GOMES, A.L.Dissertação IPEN-doc 07430