Graduated in Chemical Engineering at Faculdade Oswaldo Cruz (1983), Master in Nuclear Technology - Applications at IPEN / USP (1999), Ph.D. in Nuclear Technology - Applications at IPEN / USP (2006) and Post-Doctorate at Center for Advanced Materials ( T-CAM) from Tuskegee University, AL, USA. The main lines of research are: Synthesis of metallic nanoparticles; Obtaining and characterization of nanoparticles from mineral activity and agroindustry residues; Micro and nanofiller functionalization; Synthesis and reduction of graphene oxide; Development and modification of composite materials based on conventional and biodegradable polymers with vegetable fibers, micro and nanofillers of renewable origin; Development of biodegradable, active and intelligent plastic packaging for food, cosmetics, medical and pharmaceutical products; Development of conductive polymeric materials; Development of biomaterials for application in the regeneration of bone and dental tissue. (Text obtained from the Currículo Lattes on October 8th 2021)

Possui graduação em Engenharia Química pela Faculdade Oswaldo Cruz (1983), mestrado em Tecnologia Nuclear ? Aplicações pelo IPEN/USP (1999), doutorado em Tecnologia Nuclear ? Aplicações pelo IPEN/USP (2006) e Pós-Doutorado no Center for Advanced Materials (T-CAM) da Tuskegee University, AL, USA. As principais linhas de pesquisa são: Síntese de nanopartículas metálicas; Obtenção e caracterização de nanopartículas a partir de resíduos da atividade mineral e da agroindústria; Funcionalização de micro e nanocargas; Síntese e redução de óxido de grafeno; Desenvolvimento e modificaçao de materiais compósitos baseados em polímeros convencionais e biodegradáveis com fibras vegetais, micro e nanocargas de origem renovável; Desenvolvimento de embalagens plásticas biodegradáveis, ativas e inteligentes para alimentos, cosméticos, produtos médicos e farmacêuticos;Desenvolvimento de materiais poliméricos condutores; Desenvolvimento de biomateriais para aplicação na regeneração de tecidos ósseos e dentários. (Texto extraído do Currículo Lattes em 08 out. 2021)

Página do item completo

Resultados de Busca

Agora exibindo 1 - 1 de 1

SiOC ceramic foams synthesized from electron beam irradiated methylsilicone resin
2008 - ROCHA, R.M.; MOURA, E.A.B.; BRESSIANI, A.H.A.; BRESSIANI, J.C.
A new method to prepare silicon oxycarbide (SiOC) foams has been developed and it consists of electron beam irradiation of a methylsilicone preceramic polymer followed by pyrolysis in an inert atmosphere. Methylsilicone resin foams were prepared by simultaneous curing and foaming, without the addition of calalysts or blowing agents. The polymer precursor was irradiated with 1.5 MeV EB up to a dose of 7.0 MGy and at a dose rate of 2.8 kG/s, in air. During irradiation the polymer melted, due to rapid increase in temperature, and simultaneously crosslinked by interaction with the ionizing radiation. Crosslinking occurred mainly by poly-condensation reactions and gaseous condensation products were released. The latter acted as an intrinsic foaming agent in the molten polymer. Foams obtained with radiation doses higher than 3.5 MGy showed a high degree of crosslinking with a ceramic yield of over 89% at 1,000 °C. Pyrolysis at 1,200-1,500 °C resulted in SiOC ceramic foams with dense struts and walls, with bulk density around 0.3 g/cm3 and total porosity of 84%. Foams pyrolyzed at 1,200 °C revealed compression strength of 6.8 MPa.