Influence of Ag nanoparticles in waveguides on doped germanate glasses
Carregando...
Data
Data de publicação
2022
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
É parte de
ENCONTRO BRASILEIRO DE ESPECTROSCOPIA RAMAN, 7.
Exportar
Resumo
Writing by using femtossecond (fs) laser enables fast prototyping and has low complexity compared to other
fabrication methods. For materials that do not allow light confinement and propagation, waveguiding by double-line
technology is necessary. Previously, we demonstrated waveguiding in double-lines for undoped germanate and
tellurite glasses, as well as GeO2-PbO doped with Er3+/Yb3+ and Nd3+. The results for the Nd3+ glass were promising
for the fabrication of integrated amplifiers, lossless components and lasers. This motivated the present investigation,
where silver (Ag) nanoparticles (NPs) were added to the Nd3+ doped GeO2-PbO bulk in order to enhance its guiding
capabilities.
Raman measurements were made with a LabRam HR Evolution - HORIBA, using a 532 nm laser with 100 mW
power and a 10 x objective lens with 0.25 NA. An integration time of 1 second and 15 accumulations was used to
reduce noise and make the observed peaks clearer.
First, the Raman spectrum was measured for the bulk (b) glass (Fig. 1a) and between the written lines (Fig. 1a).
There are no substantial changes between these, indicating, as expected, that there are no relevant structural
changes in the guiding region between the two lines. However, comparing the bulk region (Fig. 1a) with the inside of
the written line with 4 superimposed lines (Fig. 1b), there are major changes in some of the peaks. The peak at
411.2 cm-1 (b) shifted to 433.9 cm-1, indicating modification in the symmetric stretching vibrations of the Ge-O-Ge
bonds. The peak at 517.5 cm-1 (b) to 508.1 cm-1 shows changes in the symmetric stretching vibrations along the Ge-
O-Ge chain, demonstrating lower density of these bonds in the irradiated region. A slight change of the 782.3 cm-1
and 867.4 cm-1 (b) are also verified, and are related to the Ge-O- and Ge-O-Ge symmetric stretching vibrations in the
GeO4 tetrahedral units and asymmetric stretching vibrations of the Ge-O-Ge bonds, respectively. These changes are
larger than the ones previously shown for the same material without the Ag NPs, which shows the influence of the
nanoparticles during the writing process.
Como referenciar
BORDON, CAMILA D.S.; DIPOLD, JESSICA; ROSSI, WAGNER de; FREITAS, ANDERSON Z.; KASSAB, LUCIANA R.P.; WETTER, NIKLAUS U. Influence of Ag nanoparticles in waveguides on doped germanate glasses. In: ENCONTRO BRASILEIRO DE ESPECTROSCOPIA RAMAN, 7., 5-8 de dezembro, 2022, São Pedro, SP. Resumo... Disponível em: http://repositorio.ipen.br/handle/123456789/33683. Acesso em: 30 Dec 2025.