Deposição eletroforética de hidroxiapatita em titânio metálico
Carregando...
Data
Data de publicação
2016
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
É parte de
CONGRESSO BRASILEIRO DE CERAMICA, 60.
Exportar
Resumo
Titanium is commonly used in the manufacture of orthopedic and dental implants due to its high corrosion resistance and good mechanical properties. However because of its grey color, the implant becomes visible due to transparency of peri-implant tissues in patients with thin gingival biotype. In this work, hydroxyapatite obtained by chemical precipitation method (Hap-S) was coated on titanium substrate by electrophoretic deposition technique, to improve implant integration in the organism and change their color. Hap-S powders were characterized by XRD, FTIR and SEM. The EPD was performed in dental grade titanium substrate with 10x10mm in dimension, at 80V, 60V and 40V for 40s, 60s and 120s. After, the coatings were dried at room temperature and sintered at 800°C for 1h. The samples were characterized by XRD and SEM. Results showed that deposition is more effective for shorter times and intermediate voltage, yielding homogeneous and crack free deposits.
Como referenciar
XAVIER, G.L.; SILVA, F.R.O.; GUGLIOTTI, C.F.; USSUI, V.; LIMA, N.B. Deposição eletroforética de hidroxiapatita em titânio metálico. In: CONGRESSO BRASILEIRO DE CERAMICA, 60., 15-18 de maio, 2016, Águas de Lindóia, SP. Anais... p. 1827-1838. Disponível em: http://repositorio.ipen.br/handle/123456789/27311. Acesso em: 27 Mar 2026.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.