Electrical properties of Cr-doped polyaniline/poly(vinylalcohol) blends
Carregando...
Data
Data de publicação
2003
Autores IPEN
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
É parte de
BRAZILIAN WORKSHOP ON SEMICONDUCTOR PHYSICS, 11th
Exportar
Resumo
Polyaniline (PANI) and their charge transfer complexes are engineering materials that continue to attract considerable attention from engineers due to its unique electrochemical behavior, environmental stability and high degree of processability. Extensive works on the preparation of electrically conductive PANI blends containing a polymeric matrix having desirable physical and good mechanical characteristics have pointed as a promising route to overcome the PANI intractabilityes. This paper reports the electrical properties of the dichromated PANI/poly(vinylalcohol) (PANI:Cr”*/PVA) blends. Doped polyaniline powder in the emeraldine base form was synthesized by the classical chemical oxidation of aniline with ammonium persulfate as the oxidant in the presence of chromium (Cr”). Annealed PANL:Cr*'/PVA was obtained by heating rate of 10°C/min and cooling rate of 5°C/min [1]. The FTIR spectroscopy revealed a structural change of both shape and intensity of the polyaniline bands after doping with chromium indicating the formation of a charge transfer complex. The SEM (Phillips XL 30) was used to understand the changes occurring in the conductivity to a microstructure level. The distribution of PANI:Cr*? (50% w/w) in the host polymer (PVA) show some tendency to occur in "flocculated structures". The samples were cut into circular shapes to form films about 500 microns thick. Electrical contacts were made with graphite adhesive [2] and the electrical d.c. measurements were done using a Keithley 237 Source Measurement Unit. We have carried out current voltage (I(V)) measurements and we inferred a capacitance about 1 nF when the resistivity was so large as 1 GQ.cm. So we have carried out capacitance-voltage (C(V)) and current voltage (I(V)) measurements in a a.c. mode. Our results indicate nonlinear behavior in the PANL:Cr'/PVA blends. We expect, trough C(V) measurements to obtain sample parameters such as dielectric constant and Schottky-type barrier height[3]. Also, from the dependence of the sample conductivity with temperature it is possible to infer the dominant conduction mechanism, i.e. band-trap activation energy, nearest neighbor and variable range hopping[4,5].
Como referenciar
SOARES, D.A.W.; SOUZA, P.H.O.; HIGA, O.Z.; RUBINGER, R.M.; QUEIROZ, A.A.A. Electrical properties of Cr-doped polyaniline/poly(vinylalcohol) blends. In: BRAZILIAN WORKSHOP ON SEMICONDUCTOR PHYSICS, 11th, Mar. 9-14, 2003, Fortaleza, CE. Abstracts... p. PS-II-57. Disponível em: http://repositorio.ipen.br/handle/123456789/21899. Acesso em: 30 Dec 2025.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.