Influence of synthesis route on phase formation and sinterability of hydroxyapatite-zirconia composites
Carregando...
Data
Data de publicação
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
Materials Science Forum
Exportar
Resumo
Reinforcement with yttria stabilized zirconia (YSZ) is an alternative to improve mechanical strength of hydroxyapatite (HAp) ceramic. However, calcium may react with zirconium to form calcium zirconate. In addition, decomposition of HAp to tricalcium phosphate (TCP) occurs with water loss inhibiting ceramic densification. In order to minimize the formation of these compounds, two synthesis routes were compared in this work: coprecipitation of hydrous yttria stabilized zirconia in a calcium phosphate gel medium and powder mixture of individual calcined powders. Composite nominal compositions were fixed at 90 and 95 HAp wt%. Calcium, zirconium and yttrium chlorides and ammonium hydrogen phosphate were the employed precursors. Ammonium hydroxide was the selected precipitation agent. Calcination was performed at 800°C for 1 hour and pellets were sintered in the range of 1150 and 1350°C for 1, 3 and 5 hours. Ceramic samples were characterized by scanning electron microscopy and apparent density measurements. Crystalline phases were quantified by Rietveld analysis of X-ray diffraction patterns. Results indicate that powders prepared by coprecipitation can cause porosity formation due to the higher chemical reactivity during synthesis process.
Como referenciar
LAZAR, D.R.R.; CUNHA, S.M.; USSUI, V.; FANCIO, E.; LIMA, N.B. de; BRESSIANI, A.H.A. Influence of synthesis route on phase formation and sinterability of hydroxyapatite-zirconia composites. Materials Science Forum, v. 591-593, p. 722-727, 2008. DOI: 10.4028/www.scientific.net/msf.591-593.722. Disponível em: http://repositorio.ipen.br/handle/123456789/4996. Acesso em: 30 Dec 2025.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.