Electric field-assisted pressureless sintering of zirconia–scandia–ceria solid electrolytes
Carregando...
Data
Data de publicação
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
Journal of Materials Science
Exportar
Resumo
Electric field-assisted (flash) pressureless sintering experiments were carried out in ZrO2 ceramics doped with 10 mol% Sc2O3 and 1 mol% CeO2 (10Sc1CeSZ). All experiments were conducted isothermally at 1050 °C for 2–5 min with the application of a 100–150 V cm−1 AC electric field at 1 kHz with 1–4 A limiting current in green compacts and in samples pre-sintered at different temperatures. Shrinkage level, structural phases and grain morphology data were collected by dilatometry, X-ray diffraction and scanning electron microscopy analyses, respectively. The results showed that for the same delivered electric power, the final shrinkage was higher for higher temperature applications of the electric field and for higher electric current pulses. Moreover, the higher the porosity, the higher the final densification of the flash-sintered 10Sc1CeSZ samples, showing that pores play a role as a preferential path in the flash sintering mechanism.
Como referenciar
MUCCILLO, ELIANA N.S.; CARVALHO, SABRINA G.M.; MUCCILLO, REGINALDO. Electric field-assisted pressureless sintering of zirconia–scandia–ceria solid electrolytes. Journal of Materials Science, v. 53, p. 1658-1671, 2018. DOI: 10.1007/s10853-017-1615-3. Disponível em: http://repositorio.ipen.br/handle/123456789/28859. Acesso em: 30 Dec 2025.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.