AISI 310 stainless steel formed by gelcasting
Carregando...
Data
Data de publicação
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
Materials Science Forum
Exportar
Resumo
This work evaluates the microstructure and the yield strength under compression at room
temperature and at 800°C of specimens prepared with AISI 310 stainless steel powder (D50 =
10 μm), manufactured by gelcasting. Parts were vacuum sintered in a single batch at 1280°C. At
room temperature, specimens presented average yield strength of 270 MPa, and at 800°C, 105 MPa.
Microstructure analysis involved the measurement of grain size along the vertical axis of cylindrical
specimens, with special attention to the effect of particles settling, and was conducted using
scanning electron and optical microscopy, and X-ray diffraction. Settling effect was assessed
considering the position where the specimen was taken and was negligible: both density and yield
strength did not vary significantly along the vertical axis.
Como referenciar
OLIVEIRA, LOUISE F.R.; NEVES, MAURICIO D.M. das; ORTEGA, FERNANDO dos S. AISI 310 stainless steel formed by gelcasting: an alternative manufacturing method. Materials Science Forum, v. 1012, p. 325-330, 2020. DOI: 10.4028/www.scientific.net/MSF.1012.325. Disponível em: http://200.136.52.105/handle/123456789/31631. Acesso em: 20 Mar 2026.