Hg0.95Re0.05Ba2Ca2Cu3O8+δ superconductor
Carregando...
Data
Data de publicação
Autores IPEN
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
Superconductor Science and Technology
Exportar
Resumo
Samples of the Hg1-xRexBa2Ca2Cu3O8+δ superconductor (Hg, Re-1223), with low rhenium (Re) content (x = 0.05), have been produced with the help of a novel thermobaric analysis technique which could monitor the total pressure inside the quartz tube during synthesis at high temperature. The sample quality was verified by means of Rietveld analysis of the x-ray diffraction data, and by ac susceptibility measurements. The formation and stability of the Hg, Re-1223 phase has also been investigated by varying the oxygen content of the Re0.05Ba2Ca2Cu3O8+δ precursor, and the mercury filling factor (ffHg = 0.00 to 0.014 g cm-3). It was observed that the reduction of oxygen content in the precursor (Re0.05Ba2Ca2Cu3O8+δ) and the increase of the mercury partial pressure inside the quartz tube enhanced the yield of the superconductor phase. Resistance measurements as a function of temperature under hydrostatic pressure (0-1.0 GPa) show an increase in the superconducting transition temperature which can be fitted with a parabolic curve. The reduction of the lattice volume induced by external hydrostatic pressure is similar to the one induced by chemical pressure due to rhenium (Re) doping (0.00
Como referenciar
ORLANDO, M.T.D.; CUNHA, A.G.; BUD´KO, S.L.; SIN, A.; MARTINEZ, L.G.; VANONI, W.; BELICH, H.; OBRADORS, X.; EMMERICH, F.G.; SAITOVITCH, E.B. Hg0.95Re0.05Ba2Ca2Cu3O8+δ superconductor: sample preparation and transport properties under hydrostatic pressure. Superconductor Science and Technology, v. 13, p. 140-147, 2000. DOI: 10.1088/0953-2048/13/2/304. Disponível em: http://repositorio.ipen.br/handle/123456789/7662. Acesso em: 30 Dec 2025.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.