Microstructure and diametral fracture strength of spark plasma sintered WC-6Co-0.2B and WC-6Co-0.5B ceramic composites from nanosized and metastable WC powders
Carregando...
Data
Data de publicação
Autores IPEN
RICARDO MENDES LEAL NETO
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
Cerâmica
Exportar
Resumo
The present work aimed at evaluating the microstructures and mechanical properties of spark plasma sintered WC-6 wt% Co ceramic
composites doped with boron (0.2 and 0.5 wt%). W-50 at% C (W-6.13 wt% C) powders produced under different milling times (20,
60, 180, and 600 min) were used as starting materials and subsequently mixed with Co (6 wt%) and B (0.2 or 0.5 wt%) powders for
5 min. The resultant WC-Co-B powder mixtures were consolidated by spark plasma sintering at 1450 °C for 10 min at 40 MPa under
vacuum in order to obtain the samples with 10 mm diameter and 3 mm thickness. The starting powders and the sintered samples
were characterized by laser diffraction particle size analysis, X-ray diffraction with Rietveld refinement, relative density, scanning
electron microscopy, energy dispersive spectrometry, Vickers hardness test, and diametral compression test. Supersaturated W solid
solution (WSS) with a crystallite size of <50 nm was formed in W-50C (at%) powder mixtures. The relative density of the sintered
composites increased with the increasing milling time up to 180 min from 79.7%±0.6% to 86.7%±0.5% for WC-6Co-0.2B and from
86.7%±0.6% to 90.9%±0.4% for WC-6Co-0.5B. Furthermore, the WC phase appeared as the matrix in the sintered samples, and
W2CoB2 precipitated homogeneously around WC grain boundaries, mainly to those containing 0.5% B. The Vickers hardness values
of the sintered WC-6Co-0.2B and WC-6Co-0.5B ranged from 1790±39 to 2158±25 HV and 1858±31 to 2182±28 HV, respectively.
The fracture strength (determined by diametral compression test) varied between 144-353 MPa due to the porosity and precipitates
in thin-thickness cylinder samples.
Como referenciar
ALENCAR E SILVA, G.S. de; LEAL NETO, R.M.; FILGUEIRA, M.; BAPTISTA, C.A.R.P.; SANTOS, C. dos; RAMOS, A.S. Microstructure and diametral fracture strength of spark plasma sintered WC-6Co-0.2B and WC-6Co-0.5B ceramic composites from nanosized and metastable WC powders. Cerâmica, v. 68, n. 386, p. 188-198, 2022. DOI: 10.1590/0366-69132022683863210. Disponível em: http://repositorio.ipen.br/handle/123456789/33397. Acesso em: 09 Apr 2026.