JOSE FERNANDO QUEIRUGA REY

Projetos de Pesquisa
Unidades Organizacionais
Cargo

Resultados de Busca

Agora exibindo 1 - 10 de 19
  • Capítulo IPEN-doc 16269
    Primary particle size effect on ohase transition in Basub(2)Insub(2)Osub(5)
    2007 - REY, J.F.Q.; FERREIRA, F.F.; MUCCILLO, E.N.S.
  • Capítulo IPEN-doc 16680
    Phase transition in Basub(2)Insub(2)Osub(5) studied by in situ high temperature X-ray diffraction using synchrotron radiation
    2009 - REY, J.F.Q.; FERREIRA, F.F.; MUCCILLO, E.N.S.
    The order-disorder phase transition in Ba,In,Os high-temperature ionic conductor was systematically studied by in situ high-temperature X-ray diffraction using synchrotron radiation and electrical conductivity. Pure barium indate was prepared by solid state reactions at 1300°C. The room-temperature structural characterization showed a high degree of phase homogeneity in the prepared material. The reduction of the order-disorder phase transition temperature was verified by electrical conductivity and high-temperature X-ray diffraction. The observed features were explained based on Fourier-transform infrared spectroscopy results that revealed the presence of hydroxyl species in the crystal lattice. The increase of the intensity of few diffraction peaks near the phase transition temperature suggests the formation of a superstructure before the orthorhombic-to-tetragonal phase transition.
  • Capítulo IPEN-doc 14483
  • Resumo IPEN-doc 16180
  • Resumo IPEN-doc 10139
    Sol gel synthesis of Ba2In2O5
    2004 - REY, J.F.Q.; MUCCILLO, E.N.S.
    Sólidos iônicos condutores de íons oxigênio têm sido extensivamente estudados devido ao seu potencial de aplicação como sensores de oxigênio, membranas permeáveis ao oxigênio, bombas de oxigênio e como eletrólitos para células de combustíveis à eletrólito sólido óxido (SOFC). Neste trabalho de pesquisa foi sintetizado o composto Ba2In2O5 por sol-gel. Para este material os valores de condutividade iônica, em condições especificas, são similares àqueles apresentados pela zircônia dopada. Na caracterização do material foram realizadas medidas de análise térmica, difração de raios X e espectroscopia de absorção na região do infravermelho, microscopia eletrônica de transmissão e varredura. Os resultados obtidos mostram todas as etapas de formação da fase, com estrutura cristalina do tipo brownmilleritta, possibilitando a redução dos tempos e temperaturas de formação da fase, quando comparado aos materiais preparados pela técnica convencional de mistura de óxidos.
  • Resumo IPEN-doc 08925
    Lattice parameters in yttria-doped ceria solid electrolytes
    2001 - REY, J.F.Q.; MUCCILLO, E.N.S.
    Cefia-rare earth solid solutions are known as solid electrolytes with potential applications in oxygen sensors and solid oxide fuel cells. Trivalcnt rare carth ions cnter finto solid solution introducing a number of anion vacancies for charge compensation. These oxygcn vacancies are quite mobile at low temperatures giving rise to a comparativcly high ionic conduction. In this study ccria-x mol% yttria solid solutions were prepared with x ranging from O to 12 by solid state reactions. These solid solutions cxhibit a fluorite-type structure with composition dcpendent lattice parameters. The variation of thc lattice parameter was studicd and corrclated with existing empirical equations based on ion packing model. The effcct of an effective ionic radius of Y3+ in eightfold coordination is also discussed.
  • Artigo IPEN-doc 09525
    Caracterizacao eletrica e microestrutural do Basub(2)Insub(2)Osub(5)
    2003 - REY, J.F.Q.; MUCCILLO, E.N.S.
  • Artigo IPEN-doc 08870
    Parametros de rede em eletrolitos solidos de ceria dopada com itria
    2002 - REY, J.F.Q.; MUCCILLO, E.N.S.
  • Tese IPEN-doc 11640
    Obtenção e caracterização do Basub(2)Insub(2)Osub(5) puro e contendo Gd e Er como aditivos
    2007 - REY, JOSE F.Q.
    Cerâmicas elétricas de Ba2In2O5 foram preparadas pelo método convencional de mistura de óxidos, e pela mistura e cristalização dos nitratos metálicos, para verificar o efeito do tamanho inicial das partículas na transição de fase ordemdesordem e na condutividade elétrica. Foram feitas substituições utilizando os cátions Gd3+ e Er3+, para verificar o efeito destes cátions na condutividade elétrica do indato de bário. Foi também preparado o óxido de índio pela técnica de complexação de cátions, e as nanopartículas obtidas foram caracterizadas por diversas técnicas. As principais técnicas de caracterização utilizadas foram: análise térmica, espectroscopia de absorção na região do infravermelho com transformada de Fourier, microscopia eletrônica de varredura, microscopia eletrônica de transmissão, difração de raios X convencional e utilizando radiação síncrotron, espalhamento de raios X a baixos ângulos, espectroscopia de energia dispersiva, espectroscopia Raman e medida da condutividade elétrica por espectroscopia de impedância. Os principais resultados mostraram que os tratamentos térmicos de calcinação e sinterização exercem forte influência na obtenção da fase Ba2In2O5. Fases espúrias são facilmente formadas no Ba2In2O5 também decorrentes da interação deste com a umidade. Um menor tamanho inicial de partículas favorece a redução na temperatura de transição de fase de segunda ordem. A introdução do Er, em teores relativamente baixos, produziu aumento na condutividade elétrica e simultânea redução na temperatura de transição de fase. Altos teores de Er e Gd dão origem a múltiplas fases. Na decomposição térmica do citrato de índio é formado um composto intermediário. A calcinação do citrato de índio produziu um material particulado com tamanho nanométrico, mesmo para temperaturas de até 900 ºC.
  • Dissertação IPEN-doc 07610