Análise dos efeitos de corrosão sob chapas de aço-carbono 1020 causadas por aerossol marinho e poluição
Carregando...
Data
Data de publicação
Autores IPEN
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
Quimica Nova
ODS
Exportar
Resumo
This work aims to analyze the effects of corrosion in different municipalities through the exposure of 1020 carbon-steel plates to the atmosphere and buried in soil. Sea air and pollution were treated as major corrosion agents and zinc has been tested to prove its effectiveness as a sacrificial anode. For this analysis, weighing and spectrophotometric methods were used to determine the iron mass loss after five months of exposure. From the data obtained, corrosion rates were calculated and compared based on different regional conditions. The results showed that the coastal region of the state of São Paulo presented higher corrosion rates compared to places of higher altitudes and further away from the sea, indicating that sea air and pollution are important agents in catalyzing the deterioration processes. In addition, zinc was efficient as a sacrificial anode, demonstrating its potential application as corrosion protection in 1020 carbon-steel plates.
Como referenciar
NOCERA, ARTHUR K.; SOUZA, GUILHERME S.; ALMEIDA, MATEUS B. de; SANTOSA, MATHEUS S.; GIL, NOEMI L.; CORREA, THAIS. Análise dos efeitos de corrosão sob chapas de aço-carbono 1020 causadas por aerossol marinho e poluição: um estudo comparativo em chapas expostas ao ambiente e em simulação de dutos subterrâneos. Quimica Nova, v. 48, n. 1, p. 1-6, 2025. DOI: 10.21577/0100-4042.20250069. Disponível em: https://repositorio.ipen.br/handle/123456789/49628. Acesso em: 29 Apr 2026.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.