Influence of the solid-state reaction method on nickel vanadate samples
Carregando...
Data
Data de publicação:
2024
Autores IPEN
Orientador
Título da Revista
ISSN da Revista
Título do Volume
É parte de
É parte de
É parte de
É parte de
BRAZIL MRS MEETING, 22nd
Exportar
Resumo
Nickel vanadate is a material increasingly used in sensors, batteries and other applications.
This work aims to obtain and stabilize nickel vanadates using the solid-state reaction
method. Three samples were synthed. Sample BI was annealed at 700°C and samples BII
and BIII at 800°C, all for 6 hours. The XRD results show that all the samples formed the
Ni3V2O8 phase, with an average crystallite of 112 nm for BI and 114 nm for BII and BIII. The
SEM data show that sample BI has spherical grains with an average of 0.573 μm, while
samples BII and BIII have rectangular grains with an of 3 μm. Given these results, the solid-state
reaction synthesis showed promising results for nickel vanadate [1]. It is hoped that
this work will contribute to turther research into these materials.
Como referenciar
CORREA, DENILSON C.; ANTUNES, MAIARA P.; COSTA, CLEIDILANE S.; PASCA, GABRIEL A.C.; BENTES, BEATRIZ A.; SILVA, CRYSTIAN W.C. da; CARBONARI, ARTUR W. Influence of the solid-state reaction method on nickel vanadate samples. In: BRAZIL MRS MEETING, 22nd, September 29 - October 3, 2024, Santos, SP. Abstract... São Carlos, SP: Aptor Software, 2024. Disponível em: https://repositorio.ipen.br/handle/123456789/48952. Acesso em: 01 Mar 2025.